Properties and applications of nanosilica-modified tooling prepregs / J. M. Nelson in SAMPE JOURNAL, Vol. 49, N° 1 (01-02/2013)  

[article]  inSAMPE JOURNAL > Vol. 49, N° 1 (01-02/2013) . - p. 7-17 Titre : Properties and applications of nanosilica-modified tooling prepregs Type de document : texte imprimé Auteurs : J. M. Nelson, Auteur ; A. M. Hine, Auteur ; D. P. Goetz, Auteur ; P. Sedgwick, Auteur ; R. H. Lowe, Auteur ; E. Rexeisen, Auteur ; R. E. King, Auteur ; C. Aitken, Auteur ; Q. Pham, Auteur Année de publication : 2013 Article en page(s) : p. 7-17 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Composites à fibres de carbone -- Propriétés mécaniques Dureté (matériaux) Epoxydes Essais (technologie) Hors autoclave (technologie) Matériaux -- Imprégnation Nanoparticules Outillage Résistance des matériaux Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Index. décimale : 668.4 Plastiques, vinyles Résumé : Recently, 3M has developed a new nanosilica-modified tooling prepreg. Fortified tooling prepreg 140°F epoxy (FTP 140F) is an out-of autoclave/autoclave-curable epoxy system which cures at low temperature and is suitable for high temperature cure cycles. This paper uses this system to examine the effect of incorporating nanosilica into tooling-specific prepreg resins on both resin and carbon fabric composites properties. Nanosilica modification using spherical nanoscale silica produces desirable changes in matrix coefficient of thermal expansion, cure shrinkage, cure exotherm, and hardness, as well as resin mechanical properties including modulus and fracture toughness. Surface hardness is quantified by both macroscale and nanoscale testing. The effect on thermal distortion of curved composite laminates is illustrated. Tooling specific enhancements include improved tool design flexibility, improved tool life, and improved dimensional stability. Real world applications of the materials are featured. Note de contenu : - The development of 3M fortified tooling prepreg 140F epoxy FTP 140F - EXPERIMENTAL : Materials and resin sample preparation - Carbon fiber composite sample preparation - RESULTS AND DISCUSSION : Summary and neat resin and composite properties 1. INCREASED DESIGN FLEXIBILITY : Improved tolerances - Reduced springback 2. IMPROVED MANUFACTURING EFFICIENCY : Improved scratch resistance - Exotherm reduction - Efficient tool build 3. TOOL LIFE IMPROVEMENT : Resistance to microcraking - Resistance to delamination - Enhanced flexural modulus after thermal cycling - APPLICATIONS : Fortified tooling prepreg bismaleimide (FTP-BMI) En ligne : http://www.nxtbook.com/nxtbooks/sampe/journal_20130102/index.php?startid=51#/8 Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=17775 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)