Effect of hexamethylene diisocyanate as compatibilizer on the mechanical properties of banana fiber/poly(butylene succinate) composites / Tetsuto Kajiyama in INTERNATIONAL POLYMER PROCESSING, Vol. XXVIII, N° 1 (03/2013)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXVIII, N° 1 (03/2013) . - p. 58-63 Titre : Effect of hexamethylene diisocyanate as compatibilizer on the mechanical properties of banana fiber/poly(butylene succinate) composites Type de document : texte imprimé Auteurs : Tetsuto Kajiyama, Auteur ; T. Yasuda, Auteur ; S. Mimoto, Auteur ; K. Shimizu, Auteur ; K. Hayashi, Auteur ; T. Yamanaka, Auteur ; M. Murakami, Auteur Année de publication : 2013 Article en page(s) : p. 58-63 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites à fibres -- Moulage par injection Composites à fibres végétales -- Propriétés mécaniques Diisocyanate d'hexaméthylène Fibres de banane Fibres végétales Hydroxyde de sodium L'hydroxyde de sodium, appelé également soude caustique7, est un corps chimique composé minéral de formule chimique NaOH, qui est à température ambiante un solide ionique. Fusible vers 318 °C, il se présente généralement sous forme de pastilles, de paillettes ou de billes blanches ou d'aspect translucide, corrosives et très hygroscopiques. Il est très soluble dans l'eau et légèrement soluble dans l'éthanol. La solution d'hydroxyde de sodium, souvent appelée soude, est une solution aqueuse transparente. Concentrée, elle est corrosive et souvent appelée lessive de soude. Les propriétés chimiques de l'hydroxyde de sodium sont surtout liées à l'ion hydroxyde HO- qui est une base forte. En outre, l'hydroxyde de sodium réagit avec le dioxyde de carbone (CO2) de l'air et se carbonate. La solubilité de la soude caustique dans l'eau augmente avec la température, à pression constante ou ambiante. Mélange Polybutylène succinate Résistance au chocs Traction (mécanique) Index. décimale : 668.4 Plastiques, vinyles Résumé : We prepared banana fiber (BF)/poly(butylene succinate) (PBS) composites using hexamethylene diisocyanate (HDI) as a compatibilizer. BF was treated with NaOH aqueous solution (BF-A). Both BF/PBS/HDI and BF-A/PBS/HDI composites were made by applying a batch type twin-kneader at 130 °C. Dumbbell specimens were prepared by an injection molding machine at 130 °C. Effect of concentration of NaOH aq on tensile strength and impact strength, effect of amount of HDI on tensile strength and Izod impact strength, and effect of mixing time on tensile strength and Izod impact strength of BF/PBS/HDI and BF-A/PBS/HDI composites were studied. When contents of HDI in composites were increased, tensile strength increased. In addition, when mixing times were increased, tensile strength increased. Although the mechanical properties of PBS were first degraded with the addition of BF, alkaline treatment to BF and the addition of HDI improved the mechanical properties. This probably due to the promotion of the adhesion between BF and PBS. The surface morphology of the fracture surfaces of the composites were observed with a scanning electron microscope (SEM). It shows that higher mechanical properties can be expected from compatibilized composites based on BF-As with aliphatic polyesters. Note de contenu : - EXPERIMENTS : Materials - Alkaline treatment of banana fiber - Mixing of materials - Molding of composites - Mechanical test of composites - SEM observation - RESULTS AND DISCUSSION : Effect of concentration of NaOH Aq on tensile properties and izod impact strength - Effect of amount of HID on tensile properties and izod impact strength - Effect of mixing time on the strength of PB/PBS/HDI DOI : 10.3139/217.2661 En ligne : https://drive.google.com/file/d/1t2_US46qJUEJIfiGIvRl5RP6cNfg9mzE/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=17765 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
14763	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)