| Titre : |
Incorporation of an acrylic fatty acid derivative as comonomer for oxidative cure in acrylic latex |
| Type de document : |
texte imprimé |
| Auteurs : |
Joana V. Barbosa, Auteur ; Jorge Moniz, Auteur ; Adélio Mendes, Auteur ; Fernà o D. Magalhà es, Auteur ; Margarida M. S. M. Bastos, Auteur |
| Année de publication : |
2014 |
| Article en page(s) : |
p. 765-773 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Acides gras
Coalescence (Sciences physiques)
Latex
Nanoparticules
Polyacryliques
Polymérisation en émulsion
Polymérisation par oxydation
Revêtements en phase aqueuse:Peinture en phase aqueuse
SiliceLa silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux.
La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...).
Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale.
Traîtements de surface
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
An acrylic fatty acid derivative (AcFAD) was evaluated as comonomer for promotion of oxidative cure in waterborne latexes. AcFAD was polymerized by solvent homopolymerization and copolymerization and by emulsion copolymerization, and the final products characterized. In the two polymerization processes, NMR analyses confirmed that the reaction occurred involving both the terminal acrylic double bond and the conjugated double bonds of the aliphatic chain. Compared with a reference acrylic latex, the results obtained after AcFAD incorporation showed a time-dependent increase in gel content and in solvent resistance of dry films. These were ascribed to oxidative cure and consequent self-crosslinking of the acrylic polymer, involving the conjugated double bonds in AcFAD side chains. Oxidative cure was also confirmed by FTIR analyses. In addition, reduction in minimum film-forming temperature evidenced that AcFAD has an internal plasticization effect during film formation. Incorporation of this comonomer in acrylic paint binder formulations constitutes a promising alternative to the use of volatile coalescing agents. |
| Note de contenu : |
- EXPERIMENTAL : 1. Materials
- Characterization methods : 1. Solution polymerization of AcFAD - 2. Emulsion copolymerization of AcFAD
- RESULTS AND DISCUSSION : 1. Solvent polymerization - 2. Emulsion polymerization |
| DOI : |
10.1007/s11998-014-9582-y |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-014-9582-y.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=22059 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 11, N° 5 (09/2014) . - p. 765-773