Cigarette smoke uptake by different woven fabrics : Analysis of mechanical and colour properties / Mahmut Kayar in COLORATION TECHNOLOGY, Vol. 140, N° 4 (08/2024)
[article]
Titre : Cigarette smoke uptake by different woven fabrics : Analysis of mechanical and colour properties Type de document : texte imprimé Auteurs : Mahmut Kayar, Auteur ; Yalcin Boztoprak, Auteur ; Belma Gjergjizi Nallbani, Auteur Année de publication : 2024 Article en page(s) : p. 585-597 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Absorption
Colorimétrie
CotonLe coton est une fibre végétale qui entoure les graines des cotonniers "véritables"(Gossypium sp.), un arbuste de la famille des Malvacées. Cette fibre est généralement transformée en fil qui est tissé pour fabriquer des tissus. Le coton est la plus importante des fibres naturelles produites dans le monde. Depuis le XIXe siècle, il constitue, grâce aux progrès de l'industrialisation et de l'agronomie, la première fibre textile du monde (près de la moitié de la consommation mondiale de fibres textiles).
Essais de résilience
Fumée de cigarette
PolyamidesUn polyamide est un polymère contenant des fonctions amides -C(=O)-NH- résultant d'une réaction de polycondensation entre les fonctions acide carboxylique et amine.
Selon la composition de leur chaîne squelettique, les polyamides sont classés en aliphatiques, semi-aromatiques et aromatiques. Selon le type d'unités répétitives, les polyamides peuvent être des homopolymères ou des copolymères.
Textiles et tissus -- Analyse
Textiles et tissus -- Propriétés mécaniques
Tissés
ViscoseIndex. décimale : 667.3 Teinture et impression des tissus Résumé : Although the impact of smoking tobacco on human health is well understood, less is known about the effects of tobacco smoke on cotton, viscose and polyamide fabrics. In this study, tobacco smoke was applied to fabric samples to investigate the effects of tobacco smoke on their mechanical and colour properties. For this purpose, tobacco smoke was pumped into a mechanism consisting of a glass box, in which cotton, viscose and polyamide fabrics were placed in a suspended position. The fabric samples were treated with tobacco smoke for 1 or 2 months. The samples were evaluated in terms of tensile and tear strength, elongation at break, as well as pilling and abrasion resistance values. A colour measurement test was used to investigate the withering effect of tobacco smoke, and Fourier Transfer–Infrared analysis was performed to examine the chemical changes. The tensile strength values in the warp direction were 419.34, 404.62 and 421.78 N without treatment and after 1 and 2 months of tobacco smoke treatment, respectively, for the cotton woven fabric. Furthermore, for woven cotton fabric, the L* value decreased from 93.8 to 78.7 after being treated with tobacco smoke for 2 months. As a result of this study, it was determined that tobacco smoke has no effect on the tensile strength properties of fabrics, causes changes to pilling and abrasion resistance values, and adversely affects the colour properties of fabrics. Note de contenu : - EXPERIMENTAL : Materials - Treating fabrics with cigarette smoke - Mechanical tests - Colour measurement - FTIR analysis
- RESULTS AND DISCUSSION : Mechanical properties - Colour properties - FTIR spectroscopyDOI : https://doi.org/10.1111/cote.12723 En ligne : https://drive.google.com/file/d/1DYOdc-ZyebrlHfeVt0plX5_47W_-gzHw/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41319
in COLORATION TECHNOLOGY > Vol. 140, N° 4 (08/2024) . - p. 585-597[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 24746 - Périodique Bibliothèque principale Documentaires Disponible