| Titre : |
UV-curable phthalazinone-based epoxy methacrylate antifouling coatings with N-vanillylnonanamide as antifoulant |
| Type de document : |
texte imprimé |
| Auteurs : |
Jin-Yan Wang, Auteur ; Ming-Xia Lv, Auteur ; Yan Kou, Auteur ; Qin-Yi Wang, Auteur ; Xi-Gao Jian, Auteur |
| Année de publication : |
2012 |
| Article en page(s) : |
p. 309-315 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Epoxydes
N-vanillylnonanamide
Phthalazinone
Polyméthacrylates
Réticulation (polymérisation)
Revêtements -- Séchage sous rayonnement ultraviolet
Revêtements antisalissures:Peinture antisalissures
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
A UV-curable solvent-free antifouling coating formulated by a novel epoxy methacrylate-containing phthalazinone moiety with reactive diluents and photoinitiator and non-toxic N-vanillylnonanamide as antifoulant was prepared. First, the basic performance of the cured films obtained was evaluated using Chinese National Standards. This environmentally friendly antifouling coating has excellent physical properties, with a pencil hardness of above 5H, an adhesion of grade 1, impact strength above 45 cm, and good resistance to alkali and salt but not acid. Then antifouling evaluation was carried out by the leaching rate of antifoulant, and by immersing samples in natural sea water, respectively. The results from the leaching rate of N-vanillylnonanamide from the antifouling coating shows that the release rate of 45 μg/m2 day of the coating with 15% antifoulant is steady after a slight decrease, and this coating can effectively prevent marine organisms attaching for 6 months, which is also evidenced by field tests in natural sea water. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Surface preparation of steel panel specimens - Preparation of the UV-curing EMA-P antifoulant coating systems and their cured films - Characterization of the cured films - Performance testing of the cured films
- RESULTS AND DISCUSSION : Formulation of the UV-curing EMP-P antifoulant coating systems - Properties of cured films - Antifouling properties of the cured films |
| DOI : |
10.1007/s11998-011-9369-3 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-011-9369-3.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=15961 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 9, N° 3 (05/2012) . - p. 309-315
Aller sur edunet
Accueil
UV-curable phthalazinone-based epoxy methacrylate antifouling coatings with N-vanillylnonanamide as antifoulant in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 9, N° 3 (05/2012)