| Résumé : |
In the present study, blown films of h-LLDPE, LDPE, and their blends were produced using a twin screw extruder. The tear properties of all films were determined in the machine direction (MD) and the transverse direction (TD). On one hand, similar values of the MD tear-resistance for the two virgin polymers, h-LLDPE and LDPE, were measured to be 100 and 120 kN/m, respectively. On the other hand, the TD tear-resistance value of h-LLDPE was 180 kN/m, four times higher than that of LDPE, 45 kN/m. It was observed that small additions of LDPE (5 to 20 wt.%) to h-LLDPE produced blends with better TD tear-resistance films, 400 kN/m. The main reason for this large increase in tear-resistance was attributed to the morphological changes induced by the addition of the LDPE polymer, as shown by SEM, FTIR, and birefringence techniques. |
Aller sur edunet
Accueil
Effect of blend ratio of h-LLDPE and LDPE on tear properties of blown films in INTERNATIONAL POLYMER PROCESSING, Vol. XXVII, N° 3 (07/2012)