Morphology influence of nanoporous nickel phosphate on intumescent flame retardant polypropylene composites / S.-B. Nie in INTERNATIONAL POLYMER PROCESSING, Vol. XXXIII, N° 4 (08/2018)

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXXIII, N° 4 (08/2018) . - p. 471-479 Titre : Morphology influence of nanoporous nickel phosphate on intumescent flame retardant polypropylene composites Type de document : texte imprimé Auteurs : S.-B. Nie, Auteur ; X. Dong, Auteur ; J.-N. Yang ; G.-L. Dai Année de publication : 2018 Article en page(s) : p. 471-479 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Calorimétrie Caractérisation Composites -- Propriétés thermiques Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Intumescence (chimie) Matériaux poreux Nanoparticules Phosphate de nickel Polypropylène Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Index. décimale : 668.4 Plastiques, vinyles Résumé : The morphology of nanoporous nickel phosphate (NP) has a close relationship with its properties, so in this work NP with needle-like and mushroom-like shape was synthesized. Then NP with needle-like and mushroom-like shape was applied in intumescent flame retardant polypropylene (PP) composites. With the addition of suitable content of NP, both mushroom-like and needle-like NP can improve the combustion and thermal properties of intumescent flame retardant PP composites. Needle-like NP shows a better thermal ant flame retardant synergist effect with intumescent flame retardants compared to mushroom-like NP. However, mushroom-like NP shows a better effect on smoke suppression. With the addition of suitable content of needle-like NP, the peak heat release rate of flame retardant PP composite decreases by 68.2 % comparing with that of the pure PP, and decreases by 23.8 % comparing with that of flame retardant PP composite without NP. The maximum weight loss temperature of PP composites can be increased from 408 °C to 485 °C with the addition of needle-like NP. Furthermore, the pyrolysis products of flame retardant PP composite with needle-like NP were investigated. From the research, it provides a further understanding of the influence on synergic effects in intumescent flame retardant systems. Note de contenu : - EXPERIMENTS : Materials - Synthesis of nanoporous nickel phosphates - Preparation of flame retardant PP composites - Characterization - RESULTS AND DISCUSSION : Characterization of NP - LOI analysis of flame retardant PP composites - Cone calorimeter test of flame retardant PP composites - Analysis of the morphology of residual char - Thermal stability investigation of flame retardant PP composites DOI : 10.3139/217.3466 Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=30886 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20077	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)