Controlled surface modification of poly(methyl methacrylate) film by fluoroalkyl end-capped vinyltrimethoxysilane oligomeric silica/hexagonal boron nitride nanocomposites |
| Type de document : |
texte imprimé |
| Auteurs : |
Jittraporn Saengkaew, Auteur ; Takahumi Ogasawara, Auteur ; Katsumi Yamashita, Auteur ; Seigo Okada, Auteur ; Suwadee Kongparakul, Auteur ; Masakazu Nishida, Auteur ; Hideo Sawada, Auteur |
| Année de publication : |
2020 |
| Article en page(s) : |
p. 643-655 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Fluorescence
Fluoropolymères
Nanoparticules
Nitrure de boreLe nitrure de bore est un composé chimique du bore et de l'azote, de formule chimique brute BN (nombre égal d'atomes de chaque élément). Le nitrure de bore est isoélectronique avec le carbone et, comme ce dernier, existe sous plusieurs formes polymorphiques, dont l'une est analogue au diamant et l'autre au graphite. La forme diamant est l'un des matériaux les plus durs connus et la forme graphite est un lubrifiant apprécié. De plus, ces deux polymorphes possèdent des propriétés d'absorption radar.
Oléophobie
Oligomères
Polyméthacrylate de méthyleLe poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec.
Revêtements organiques
Traîtements de surface
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Fluoroalkyl end-capped vinyltrimethoxysilane oligomer [RF-(CH2CHSi(OMe)3)n-RF; n = 2, 3; RF = CF(CF3)OC3F7] undergoes sol–gel reactions in the presence of hexagonal boron nitride (h-BN) nanoparticles under alkaline or acidic conditions at room temperature to afford the corresponding fluorinated oligomeric silica/h-BN nanocomposites in good isolated yields (~ 80%), respectively. The fluorinated oligomeric silica/h-BN nanocomposites thus obtained were found to exhibit a good dispersibility toward the traditional organic media including water. These two kinds of fluorinated nanocomposites were applied to the surface modification of poly(methyl methacrylate) (PMMA). The fluorinated nanocomposites prepared under alkaline conditions can give not only a good oleophobic characteristic imparted by longer fluoroalkyl groups in the composites but also the higher fluorescent emission related to the presence of h-BN on the only surface side of the modified PMMA film. In contrast, the fluorinated nanocomposites prepared under acidic conditions can provide a good oleophobic characteristic and a higher fluorescent emission on both the surface and even on the reverse side of the PMMA film. Such unique controlled surface modification ability will be discussed by 29Si solid-state NMR spectra of these two types of the nanocomposites. |
| Note de contenu : |
- EXPERIMENTAL : Materials
- MATERIALS : Preparation of fluoroalkyl end-capped vinyltrimethoxysilane oligomeric silica/hexagonal boron nitride nanocomposites [RF-(VM-SiO2)n-RF/h-BN] - FTIR spectra measurements
of the RF-(VM-SiO2)n-RF nanoparticles, and the RF-(VM-SiO2)n-RF/h-BN composites - Preparation of modified PMMA films treated with the RF-(VM-SiO2)n-RF/h-BN nanocomposites |
| DOI : |
https://doi.org/10.1007/s11998-019-00261-y |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-019-00261-y.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34096 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 3 (05-06/2020) . - p. 643-655
Aller sur edunet
Accueil
Ajouter le résultat dans votre panier Affiner la rechercheAmorphous low molecular weight aromatic compounds possessing no weight loss behavior in fluoroalkyl end-capped vinyltrimethoxysilane oligomeric silica/hexagonal boron nitride nanocomposites even after calcination at 800°C in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 17, N° 4 (07/2020)