Influence of some vegetable oils on the photocrosslinking of coatings based on an o-cresol novolac epoxy resin and a bis-cycloaliphatic diepoxide |
| Type de document : |
texte imprimé |
| Auteurs : |
Le Xuan Hien, Auteur ; Do Thi Ngoc Minh, Auteur ; Trieu Nguyen Thi Viet, Auteur ; Christian Decker, Auteur |
| Année de publication : |
2011 |
| Article en page(s) : |
p. 343-353 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Cinétique chimique
Epoxydes
Huiles et graisses végétales
Résines photoréticulables
Réticulation (polymérisation)
Revêtements
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
The influence of cashew nut shell oil (CNO), epoxidized soybean oil (ESO), castor oil (CO), and dioctyl phtalate (DOP) on the photocrosslinking kinetics of UV curable mixtures containing an o-cresol novolac epoxy resin (CNE), a bis-cycloaliphatic diepoxide monomer (BCDE), and a triarylsulfonium salt (TAS) as a cationic photoinitiator has been studied. The formulation with a weight ratio CNE/BCDE/TAS of 60/40/5 was found to have the highest cure rate and the greatest final conversion of epoxy groups upon UV exposure. The presence of an unsaturated oil or of DOP in the UV curable formulation, at a content ranging from 0.07 to 0.79 mol/kg, was shown to increase the initial polymerization rate of the epoxy groups from 12 up to 31 mol/kg s, and the epoxy conversion after 18 s UV exposure from 80 up to 95%. It was found that the UV cured coatings containing CNO or DOP at concentrations between 0.3 and 0.6 mol/kg and ESO at concentrations between 0.12 and 0.19 mol/kg exhibit the best performance. These results were explained by a number of competitive factors, mainly the effects of the chemical structure and content of the oils and of DOP on the polarity, viscosity, compatibility, and internal filter effect of the UV curable resins, as well as by the characteristics of the tridimensional polymer networks formed upon UV exposure. The materials produced under the optimal conditions determined in this study can be used as high performance decorative and protective coatings and also as adhesives in different sectors of applications. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Samples preparation - Irradiation - Analysis (IR analysis - Determination of the gel fraction and of the swelling degree - Determination of the viscosity - Determination of the physico-mechanical properties - Thermogravimetric).
- RESULTS AND DISCUSSION : Kinetic study (mechanism of the photoinitiated cationic polymerization - UV curing of the systems without plasticiser - UV curing of the systems containing plasticizer) - Properties of UV-cured coatings (without plasticiser - With plasticizers). |
| DOI : |
10.1007/s11998-010-9303-0 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-010-9303-0.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=11674 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 8, N° 3 (05/2011) . - p. 343-353
Aller sur edunet
Accueil
Influence of some vegetable oils on the photocrosslinking of coatings based on an o-cresol novolac epoxy resin and a bis-cycloaliphatic diepoxide in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 8, N° 3 (05/2011)