Preparation of high-hardness silicon-based antireflective optical coatings at low temperature and without calcination / Feifei Xu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 5 (09/2024)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 5 (09/2024) . - p. 1819-1829 Titre : Preparation of high-hardness silicon-based antireflective optical coatings at low temperature and without calcination Type de document : texte imprimé Auteurs : Feifei Xu, Auteur ; Xin Dong, Auteur ; Qian Jia, Auteur ; Ruoyu Chen, Auteur Année de publication : 2024 Article en page(s) : p. 1819-1829 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Organosilanes Orthosilicate de tétraéthyle L'orthosilicate de tétraéthyle (TEOS) est un composé chimique de formule Si(OCH2CH3)4 ou plus simplement Si(OEt)4; l'abréviation TEOS (pour tetraethylorthosilicate) est généralement utilisée dans l'industrie du sol-gel, où il est intensivement étudié. La majorité des études en sol-gel pour des sols de silices ont utilisé ce produit comme précurseur. Le TEOS est généralement produit par alcoolyse du tétrachlorure de silicium SiCl4 dans de l'éthanol CH3CH2OH : SiCl4 + 4 CH3CH2OH → Si(OCH2CH3)4 + 4 HCl. Il est utilisé pour la réticulation de silicones et possède certaines applications comme précurseur du dioxyde de silicium SiO2 dans l'industrie des semi-conducteurs6 dans le cadre d'une réaction sol-gel. La propriété remarquable du TEOS est en effet de former du SiO2 par simple hydrolyse en libérant de l'éthanol CH3CH2OH : Si(OCH2CH3)4 + 2 H2O → SiO2 + 4 CH3CH2OH. Perfluoroalkyles Polyméthacrylate de méthyle Le poly(méthacrylate de méthyle) (souvent abrégé en PMMA, de l'anglais Poly(methyl methacrylate)) est un polymère thermoplastique transparent obtenu par polyaddition dont le monomère est le méthacrylate de méthyle (MMA). Ce polymère est plus connu sous son premier nom commercial de Plexiglas (nom déposé), même si le leader global du PMMA est Altuglas International9 du groupe Arkema, sous le nom commercial Altuglas. Il est également vendu sous les noms commerciaux Lucite, Crystalite, Perspex ou Nudec. Résistance à l'usure Revêtement antireflet Revêtements -- Propriétés mécaniques Revêtements -- Propriétés optiques Index. décimale : 667.9 Revêtements et enduits Résumé : Mechanical strength is an important factor that affects and limits the life of surface antireflective (ARC) coatings such as optical lenses, photovoltaic panels, and liquid crystal displays. In this work, a network-structured silica sol was prepared using tetraethyl orthosilicate (TEOS) and methyltriethoxysilane as silicon sources. Triethoxy(1H,1H,2H,2H-nonafluorohexyl)silane (C4FTES) was used to modify the acid-catalyzed silica sol. Finally, the mixed sol was plated on the surface of polymethyl methacrylate by impregnation-pulling method. The coating obtained after drying at 100°C showed a maximum transmittance of 97.98% in the visible wavelength range (400–800 nm). The coating still maintained good optical properties after undergoing various wear-resistant tests such as sandpaper abrasion and cotton ball friction. Moreover, the pencil hardness test of the coating improved from 5B to 3H after it was modified by short-chain perfluoroalkyl groups (C4FTES). This work required only low-temperature treatment without calcination to prepare a silicon-based ARC coating formed by copolymerization of C4FTES and TEOS, and the mechanical properties of the coating meet actual needs. This easy-to-operate preparation method greatly expands the application scope of silicon-based ARC coatings in the field of heat-sensitive materials. Note de contenu : - EXPERIMENTAL SECTION : - Materials - Preparation of alkali-catalyzed silica sol - Preparation of acid-catalyzed silica sol - Preparation of mixed sols - Characterization - Performance tests - RESULTS AND DISCUSSION : - Molecular structures of the sols - Microstructure of the sols - Optical properties and microstructure of the coatings - Mechanical properties of the coatings DOI : https://doi.org/10.1007/s11998-024-00940-5 En ligne : https://drive.google.com/file/d/1EF6zun0FM1DT73WgaH8YnFVDGqXPvxSj/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41530 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24844	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)