Chloride transmission in silane composite emulsion-protected concrete under the coupling effect of flexural loading and wetting–drying cycles / Mengjun Hu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 3 (05/2024)
[article]
inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 3 (05/2024) . - p. 1017-1030
Titre : Chloride transmission in silane composite emulsion-protected concrete under the coupling effect of flexural loading and wetting–drying cycles Type de document : texte imprimé Auteurs : Mengjun Hu, Auteur ; Shaochun Li, Auteur ; Xu Chen, Auteur ; Shiyu Sui, Auteur ; Yongjuan Geng, Auteur ; Jialin Jiang, Auteur ; Zhijun Liu, Auteur Année de publication : 2024 Article en page(s) : p. 1017-1030 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Chlorures
Essais (technologie)
Isobutyltriethoxysilane
Matériaux cimentaires -- Revêtements protecteurs
Orthosilicate de tétraéthyleL'orthosilicate de tétraéthyle (TEOS) est un composé chimique de formule Si(OCH2CH3)4 ou plus simplement Si(OEt)4; l'abréviation TEOS (pour tetraethylorthosilicate) est généralement utilisée dans l'industrie du sol-gel, où il est intensivement étudié. La majorité des études en sol-gel pour des sols de silices ont utilisé ce produit comme précurseur.
Le TEOS est généralement produit par alcoolyse du tétrachlorure de silicium SiCl4 dans de l'éthanol CH3CH2OH :
SiCl4 + 4 CH3CH2OH → Si(OCH2CH3)4 + 4 HCl.
Il est utilisé pour la réticulation de silicones et possède certaines applications comme précurseur du dioxyde de silicium SiO2 dans l'industrie des semi-conducteurs6 dans le cadre d'une réaction sol-gel. La propriété remarquable du TEOS est en effet de former du SiO2 par simple hydrolyse en libérant de l'éthanol CH3CH2OH :
Si(OCH2CH3)4 + 2 H2O → SiO2 + 4 CH3CH2OH.
Oxyde de graphène
Réaction de couplage
Revêtements en phase aqueuse
Revêtements organiques
SilanesIndex. décimale : 667.9 Revêtements et enduits Résumé : The coupling effect of flexural loading and wetting–drying cycles on chloride transmission in silane composite emulsion-protected concrete is presented in this paper. Graphene oxide/isobutyltriethoxysilane (GS) and tetraethyl orthosilicate/isobutyltriethoxysilane (TS) composite emulsion was prepared to obstruct the penetration of chloride, and the influence of flexural loading and exposure time on the protective effect were mainly considered. The results show that the content and diffusion coefficient of chloride are affected significantly by flexural loading, exposure age, and protective emulsion. Loads with different stress ratios affect the internal transmission of chloride by changing the compactness of concrete. The prolongation of the exposure age leads to the accumulation of chloride, thereby increasing the internal chloride contents of concrete. The GS/TS composite emulsion reacts with the hydration products to form the hydrophobic layer, which can significantly prevent the penetration of chloride. In particular, the protective performance of GS under low stress ratios is better than that of TS, while under high stress levels, TS has better resistance to chloride erosion. Relatively speaking, the long-term protective effect of GS is better than that of TS. Note de contenu : - MATERIALS AND METHODS : Materials - Test methods
- RESULTS AND DISCUSSION : The content of chloride in silane-protected concrete subjected to flexural loading and wetting-drying cycles - Diffusion coefficient of chloride in silane-protected concrete subjected to flexural loading and wetting-drying cycles
- Table 1 : Chemical composition of cement (%)
- Table 2 : Materials for preparing the silane composite emulsions
- Fig. 1 : Preparation of composite emulsionDOI : https://doi.org/10.1007/s11998-023-00869-1 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-023-00869-1.pdf Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41074 [article]Réservation