A comparative study on adhesive properties of nanoparticle reinforced epoxy bonded single-strap repaired composites / Harun Karaoglan in INTERNATIONAL POLYMER PROCESSING, Vol. 39, N° 1 (2024)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. 39, N° 1 (2024) . - p. 70-79 Titre : A comparative study on adhesive properties of nanoparticle reinforced epoxy bonded single-strap repaired composites Type de document : texte imprimé Auteurs : Harun Karaoglan, Auteur ; Ahmet Erklig, Auteur ; Nurettin Furkan Dogan, Auteur ; Mehmet Bulut, Auteur Année de publication : 2024 Article en page(s) : p. 70-79 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Argile Collage Colles:Adhésifs Composites à fibres de verre Entretien et réparations Epoxydes Graphène Le graphène est un cristal bidimensionnel (monoplan) de carbone dont l'empilement constitue le graphite. Il a été isolé en 2004 par Andre Geim, du département de physique de l'université de Manchester, qui a reçu pour cette découverte le prix Nobel de physique en 2010 avec Konstantin Novoselov. Il peut être produit de deux manières : par extraction mécanique du graphite (graphène exfolié) dont la technique a été mise au point en 2004, ou par chauffage d'un cristal de carbure de silicium, qui permet la libération des atomes de silicium (graphène epitaxié). Record en conduction thermique jusqu'à 5300 W.m-1.K-1. C'est aussi un matériaux conducteur. Nanoparticules Patchs de réparation Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Index. décimale : 668.4 Plastiques, vinyles Résumé : This study aimed to evaluate the impact of nanoparticle inclusion and patch size on the bonding performance of single-strap repaired glass-reinforced composite plates through experimental investigations. Epoxy adhesive was modified with three different nanoparticles: nano-silica (NS), nano-graphene (NG), and nano-clay (NC) at varying weight contents. The patch repair performance of the test samples was evaluated using two patch ratios (Patch diameter (D)/Hole diameter (d) = 2 and 3) to explore the influence of patch size on repair effectiveness. GFRP composite base plates having a 10 mm diameter hole in the middle were patch repaired by using patches with the same material. Tensile tests were conducted to compare the tensile performance of the repaired composite samples, and the results were compared with the samples with and without holes. Based on the findings, it was noted that samples with a larger patch ratio (D/d = 3) can withstand higher tensile loads compared to those with a patch ratio of 2. Moreover, it was found that the specimen repaired with 3 % by weight NC-filled epoxy adhesive showed the greatest increase in tensile load value. This increase was recorded at both patch rates, with a percentage improvement of 2.8 and 19.54 % compared to pure epoxy adhesive. Also, it was observed that when the patch ratio was 3, the 3 % NS-filled adhesive showed an increase of 3.3 %. On the other hand, all combinations of NG-filled adhesive showed a decrease in maximum tensile load values. Note de contenu : - Materials and methods : Manufacturing of the test samples - Tensile test - Results and discussion : NS inclusion effects - NC particle inclusion effects - NG particle inclusion effects DOI : https://doi.org/10.1515/ipp-2023-4396 En ligne : https://drive.google.com/file/d/1YyRmQzDwPxf6gkgjUlHKcQlSUZsJ_GLu/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40852 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24673	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)