Corrosion-resistant super-amphiphobic (PVDF-fnAl2O3) coating with thermal and mechanical stability / Nadiah Ghazali in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 2 (03/2024)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 2 (03/2024) . - p. 589-599 Titre : Corrosion-resistant super-amphiphobic (PVDF-fnAl2O3) coating with thermal and mechanical stability Type de document : texte imprimé Auteurs : Nadiah Ghazali, Auteur ; Wan Jefrey Basirun, Auteur ; Azmi Mohammed Nor, Auteur ; Mohd Rafie Johan, Auteur ; Fariza Abdul Rahman, Auteur Année de publication : 2024 Article en page(s) : p. 589-599 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Alumine Amphiphobie Anticorrosifs Anticorrosion Caractérisation Fluoroalkylsilane Hydrophobie Mouillabilité Polyfluorure de vinylidène Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : The thermal and mechanical stability of amphiphobic anti-corrosion coating is evaluated in this study. The coating was fabricated from functionalized nano Al2O3 and polyvinylidene fluoride (PVDF) and analyzed using FTIR, DSC, TGA, XRD, abrasion and cross-hatched adhesion test analyses. DSC and XRD revealed the presence of multiple crystalline phases of PVDF in the coating which eventually increased the crystallinity and melting temperature. The removal of the CFx chain from alkylsilane occurred at elevated temperatures, which decreased the repellent characteristic. Overall, the coating demonstrated good thermal stability until the temperature of 450°C with the ISO class 2 adhesion. Note de contenu : - EXPERIMENTAL METHODS : Materials - Experimental procedure - Characterization - RESULTS AND DISCUSSION : Coating wettability - Corrosion rate - Chemical composition and phase evaluation - Thermal properties - Mechanical properties - Table 1 : The PVDF and FAS characteristic bands and the corresponding PVDF crystalline phases - Table 2 : The melting temperature (Tm), melting enthalpy (H) and the calculated degree of crystallinity (Xc) for the single and double heating cycles - Table 3 : The cross-hatched test performed on three different points for PVDF base and coating sample En ligne : https://drive.google.com/file/d/144homJFiYz54fN8noyr-smA7iLTySSyf/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40779 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24736	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)