Development of an epoxy-based self-intumescent fire protective coating containing an appropriate mass ratio of APP and Cu2O / Chengshou Zhao in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 2 (03/2024)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 2 (03/2024) . - p. 547-558 Titre : Development of an epoxy-based self-intumescent fire protective coating containing an appropriate mass ratio of APP and Cu2O Type de document : texte imprimé Auteurs : Chengshou Zhao, Auteur ; Yisong Jiang, Auteur ; Wang Fu, Auteur ; Zhuangyuan Liu, Auteur ; Siyuan Liu, Auteur ; Huaqiao Peng, Auteur ; Nima Esmaeili, Auteur Année de publication : 2024 Article en page(s) : p. 547-558 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Caractérisation Epoxydes Formulation (Génie chimique) Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Intumescence (chimie) Métaux -- Revêtements protecteurs Oxyde de cuivre Polyphosphate d'ammonium Index. décimale : 667.9 Revêtements et enduits Résumé : A novel epoxy-based self-intumescent fire protective coating has been developed by formulating a combination of ammonium polyphosphate (APP) and copper (I) oxide (Cu2O) in epoxy resin (EP). The effects of various combinations on fire protective performance for steel plate were evaluated using a lab-scale simulated big panel test. Formulations with different mass ratios of APP to Cu2O ranging from 10:0 to 2:8 exhibit good fire protective performance for steel plate. While the final equilibrium backside temperature of un-protected steel plate reached 529 °C, it did not exceed 282 °C for the protected plates with 2 mm thick coatings, which is much lower than the failure temperature of steel (ca. 500 °C). The lowest final equilibrium backside temperature of coated steel plate was 234.5 °C for the optimal formulation (EP/24APP/16Cu2O) with an APP/Cu2O mass ratio of 6/4 in EP. Interestingly, the limiting oxygen index (LOI) value (46.8%) for the optimized formulation (EP/24APP/16Cu2O) is not the highest, being lower than those of (EP/40APP/0Cu2O) and (EP/32APP/8Cu2O) formulations. The fire behavior of the optimized formulation (EP/24APP/16Cu2O) and control EP was compared using the cone calorimetry. The main fire hazard parameters such as peak heat release rate, total smoke production and peak CO production for EP/24APP/16Cu2O are reduced by 80.0%, 59.5% and 75.0%, respectively, relative to those for EP. This indicates that the EP/24APP/16Cu2O formulation provides significantly better fire safety than does control EP alone. A possible mode of action for the combination of APP/Cu2O in terms of the expansion ratio and heat insulation degree of the formed intumescent char layer may be proposed. Thus, this work contributed a reference for developing intumescent fire protective coating with high fire safety. Note de contenu : - EXPERIMENTAL : Materials - Coating preparation - Characterization - RESULTS AND DISCUSSION : Fire protection - Flame retardance - Combustion performance - Possible fire protective action mode - Table 1 : Formulations of different coatings - Table 2 : Cone calorimeter parameters of EP and EP/24APP/16Cu2O DOI : https://doi.org/10.1007/s11998-023-00837-9 En ligne : https://drive.google.com/file/d/1ima9p-v-zHkpIR2kHCr_ft89fzeZ3UFm/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40776 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24736	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)