Enhanced wear resistance of epoxy coatings on steel using graphene oxide / Amanda B. Filizzola in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 1 (01/2024)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 1 (01/2024) . - p. 215-228 Titre : Enhanced wear resistance of epoxy coatings on steel using graphene oxide Type de document : texte imprimé Auteurs : Amanda B. Filizzola, Auteur ; Joao L. N. Pereira, Auteur ; Pollyanna R. dos Santos, Auteur ; Felipe da S. Medeiros, Auteur ; Sthéfany Z. S. do Amparo, Auteur ; Claudia K. B. de Vasconcelos, Auteur ; Glaura G. Silva, Auteur Année de publication : 2024 Article en page(s) : p. 215-228 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Abrasion Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Epoxydes Flexion (mécanique) Métaux -- Revêtements Mouillabilité Oxyde de graphène Résistance à l'usure Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : Graphene oxide (GO) addition to epoxy can improve various properties provided that the GO features, dispersion and interaction with epoxy are optimized. Herein, the challenge of improving the hydrophobicity, flexural behavior and wear resistance of an epoxy coating on steel substrate was addressed by GO incorporation. Three GO concentrations were tested in the epoxy system (0.1, 0.25, and 0.50% m/m), and nanocomposites were prepared via roller mill. An increase in the thermal stability of the pure epoxy by 23°C was observed for the nanocomposites as a function of GO incorporation. XPS analyses were carried out to study the interaction between DGEBA and GO, and the results show that a covalent link was formed between GO and epoxy. The wettability test showed an increase of 26° in the contact angle while the behavior of the system from mechanical bending tests showed gains of 52% in the energy to fracture for the sample containing 0.5 wt.% GO with respect to the neat epoxy. The wear of the coatings showed a 31% decrease in the wear coefficient of the nanocomposite compared to the reference. The set of results reported in the present work pointed to the epoxy/GO coating as promising in terms of hydrophobicity and wear properties. Note de contenu : - Chemicals and reagents - Synthesis of GO - Nanocomposite coating preparation and application on the substrate - Characterization - Table 1 : Chemical composition (wt.%) of the steel substrate - Table 2 : Elementary analysis for the GO sample - Table 3 : Glass transition temperature and percentage of cure of the samples under study obtained by DSC in triplicate - Table 4 :- Binding energy and percentage of the components from C1s, O1s and N1s XPS spectra for epoxy and epoxy-GO samples DOI : https://doi.org/10.1007/s11998-023-00811-5 En ligne : https://drive.google.com/file/d/1mChElztnOwMgBPz0JSjniPQ_xRRrimnN/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40442 [article]

Réservation

Réserver ce document

Exemplaires (2)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24443	-	Périodique	Bibliothèque principale	Documentaires	Disponible
24735	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)