Dyeing properties of polylactic acid fabric with disperse dyes of different structures using decamethylcyclopentasiloxane as non-aqueous media / Yinchun Fang in COLORATION TECHNOLOGY, Vol. 140, N° 1 (02/2024)  

[article]  inCOLORATION TECHNOLOGY > Vol. 140, N° 1 (02/2024) . - p. 52-60 Titre : Dyeing properties of polylactic acid fabric with disperse dyes of different structures using decamethylcyclopentasiloxane as non-aqueous media Type de document : texte imprimé Auteurs : Yinchun Fang, Auteur ; Jianguo Wu, Auteur ; Guojie Ma, Auteur ; Qufu Wei, Auteur Année de publication : 2024 Article en page(s) : p. 52-60 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Colorants dispersés Catégorie de colorants très peu solubles dans l'eau, utilisés à l'origine comme colorants pour l'acétate, et qui généralement sont appliqués sous forme de suspensions aqueuses de faible concentration.Les colorants dispersés sont largement utilisés dans la teinture de la plupart des fibres manufacturées, surtout le polyester. Décaméthylcyclopentasiloxane Polylactique, Acide L'acide polylactique (anglais : polylactic acid, abrégé en PLA) est un polymère entièrement biodégradable utilisé dans l'alimentation pour l'emballage des Å“ufs et plus récemment pour remplacer les sacs et cabas en plastiques jusqu'ici distribués dans les commerces. Il est utilisé également en chirurgie où les sutures sont réalisées avec des polymères biodégradables qui sont décomposés par réaction avec l’eau ou sous l’action d’enzymes. Il est également utilisé pour les nouveaux essais de stent biodégradable. Le PLA peut-être obtenu à partir d'amidon de maïs, ce qui en fait la première alternative naturelle au polyéthylène (le terme de bioplastique est utilisé). En effet, l'acide polylactique est un produit résultant de la fermentation des sucres ou de l'amidon sous l'effet de bactéries synthétisant l'acide lactique. Dans un second temps, l'acide lactique est polymérisé par un nouveau procédé de fermentation, pour devenir de l'acide polylactique. Ce procédé conduit à des polymères avec des masses molaires relativement basses. Afin de produire un acide polylactique avec des masses molaires plus élevées, l'acide polylactique produit par condensation de l'acide lactique est dépolymérisé, produisant du lactide, qui est à son tour polymérisé par ouverture de cycle. Le PLA est donc l’un de ces polymères, dans lequel les longues molécules filiformes sont construites par la réaction d’un groupement acide et d’une molécule d’acide lactique sur le groupement hydroxyle d’une autre pour donner une jonction ester. Dans le corps, la réaction se fait en sens inverse et l’acide lactique ainsi libéré est incorporé dans le processus métabolique normal. On obtient un polymère plus résistant en utilisant l'acide glycolique, soit seul, soit combiné à l’acide lactique. Teinture -- Fibres textiles synthétiques Index. décimale : 667.3 Teinture et impression des tissus Résumé : Polylactic acid (PLA) fibre, as a renewable and biodegradable synthetic polymer, is attracting increasing attention in the field of textiles. However, there are still some problems associated with PLA fibre dyeing, with a traditional water bath using disperse dyes restricting its industrialisation. Waterless dyeing, as a green and environmentally friendly dyeing method for PLA fibre, is expected to replace the traditional water bath dyeing method. However, the disperse dyes suitable for PLA fibre are different from those that are suitable for traditional poly(ethylene terephthalate) fibre. In the current study, the waterless dyeability of PLA fibre using disperse dyes with different chemical structures, and decamethylcyclopentasiloxane (D5) as the media, was investigated. First, the optimal dyeing process conditions of dye concentration, dyeing temperature, dyeing time and liquor ratio for PLA waterless dyeing were determined. The results indicated that the most suitable dyeing process conditions were: a dye concentration of 5%, dyeing temperature and time of 120°C and 40 minutes, respectively, and a liquor ratio of 1:10. Next, PLA was dyed with 10 disperse dyes with different structures using the determined optimum dyeing process conditions to compare their dyeing properties. The results showed that there were obvious differences in the K/S values for PLA dyed with dyes of different structures. The K/S values for PLA dyed with monoazo structure dyes were significantly higher than those for anthraquinones and heterocyclic structure dyes. Disperse dyes with a monoazo structure are suitable for PLA waterless dyeing. This study provides a research basis to develop suitable dyes for waterless dyeing PLA using D5 as the media. Note de contenu : - EXPERIMENTAL : Materials - Dyeing process - Characterisation - RESULTS AND DISCUSSION : Optimisation of the dyeing process conditions - Dyeing property of PLA with disperse dyes of different structures - Table 1 : Chemical structure classes of disperse dyes - Table 2 : Dyeing properties and tensile strength of polylactic acid (PLA) with different dye concentration - Table 3 : Dyeing properties and tensile strength of polylactic acid (PLA) with different dyeing temperatures - Table 4 : Dyeing properties and tensile strength of polylactic acid (PLA) with different dyeing times - Table 5 : Dyeing properties and tensile strength of polylactic acid (PLA) with different liquor ratios - Table 6 : Dyeing properties and tensile strength of polylactic acid (PLA) fabrics with disperse dyes of different chemical structures DOI : https://doi.org/10.1111/cote.12693 En ligne : https://drive.google.com/file/d/1iUqSSQNRccY141zx2H3N5ljcLzn4vVCA/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40390 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24413	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)