Preparation of underwater superoleophobic SiO2/CS/PVA coating on 304 stainless-steel mesh with excellent oil-water separation performance and stability / Pu Gong in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 6 (11/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 6 (11/2023) . - p. 2101-2112 Titre : Preparation of underwater superoleophobic SiO2/CS/PVA coating on 304 stainless-steel mesh with excellent oil-water separation performance and stability Type de document : texte imprimé Auteurs : Pu Gong, Auteur ; Enyang Liu, Auteur ; Sirong Yu, Auteur ; Kang Wang, Auteur ; Wei Li, Auteur ; Mingshan Zhang, Auteur ; Yuanji Song, Auteur ; Huaisen Li, Auteur ; Daijun Sun, Auteur ; Wei Xiong, Auteur ; Bingying Wang, Auteur Année de publication : 2023 Article en page(s) : p. 2101-2112 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier inoxydable Alcool polyvinylique Chitosane Le chitosane ou chitosan est un polyoside composé de la distribution aléatoire de D-glucosamine liée en ß-(1-4) (unité désacétylée) et de N-acétyl-D-glucosamine (unité acétylée). Il est produit par désacétylation chimique (en milieu alcalin) ou enzymatique de la chitine, le composant de l'exosquelette des arthropodes (crustacés) ou de l'endosquelette des céphalopodes (calmars...) ou encore de la paroi des champignons. Cette matière première est déminéralisée par traitement à l'acide chlorhydrique, puis déprotéinée en présence de soude ou de potasse et enfin décolorée grâce à un agent oxydant. Le degré d'acétylation (DA) est le pourcentage d'unités acétylées par rapport au nombre d'unités totales, il peut être déterminé par spectroscopie infrarouge à transformée de Fourier (IR-TF) ou par un titrage par une base forte. La frontière entre chitosane et chitine correspond à un DA de 50 % : en deçà le composé est nommé chitosane, au-delà, chitine. Le chitosane est soluble en milieu acide contrairement à la chitine qui est insoluble. Il est important de faire la distinction entre le degré d'acétylation (DA) et le degré de déacétylation (DD). L'un étant l'inverse de l'autre c'est-à-dire que du chitosane ayant un DD de 85 %, possède 15 % de groupements acétyles et 85 % de groupements amines sur ses chaînes. Le chitosane est biodégradable et biocompatible (notamment hémocompatible). Il est également bactériostatique et fongistatique. Le chitosane est également utilisé pour le traitement des eaux usées par filtration ainsi que dans divers domaines comme la cosmétique, la diététique et la médecine. Dioxyde de silicium Dip-coating Métaux -- Revêtements protecteurs Oléophobie Revêtements -- Stabilité Revêtements organiques Séparation huile/eau Index. décimale : 667.9 Revêtements et enduits Résumé : The wide application prospect of super-wetting materials in the field of oil–water separation has aroused extensive scholarly interest. With the aid of SEM, EDS, and FTIR, it was proved that the SiO2/CS/PVA underwater superoleophobic coating was successfully prepared by etching and dip coating. The surface of the coating formed a mountain-like microstructure and with the extension of etching time, the roughness of the mountain-like microstructure increased. After more than 10 min of etching, the roughness of microstructure was basically unchanged and the underwater OCA was as high as 160.3°. The results indicated that 10 min was the best time for etching reaction. The performance of oil–water separation was tested. The separation efficiency after 50 separation cycles was still more than 98.5%. The results showed that the coating had excellent oil–water separation performance and separation cycle characteristics. The stability of the SiO2/CS/PVA underwater superoleophobic coating was tested. After being placed in acidic solution, alkaline solution or air, the underwater OCA of the coating was higher than 155° and the oil–water separation efficiency was as high as 98%. The experimental results proved the excellent long-term and pH stability. In addition, the coating had self-cleaning ability and low adhesion performance, which can arrest oil phase pollution. Note de contenu : - EXPERIMENTAL : Materials - Preparation of SiO2/CS/PVA underwater superoleophobic coating - RESULTS AND DISCUSSION : Interaction of CS/PVA/GA - Chemical composition - Micromorphology - Wettability - Low adhesion property - Self-cleaning property - Oil-water separation performance - Stability of SiO2/CS/PVA coating DOI : https://doi.org/10.1007/s11998-023-00807-1 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-023-00807-1.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40185 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24337	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)