Titre : |
Influence of different dispersants on the quality and stability of aqueous quinacridone magenta pigment dispersion for ink-jet applications |
Type de document : |
texte imprimé |
Auteurs : |
Rafal Gaida, Auteur ; Kararzyna Dziubek, Auteur ; Katarzyna Krol, Auteur ; Monika Ostaszewska, Auteur ; Marian Wit, Auteur |
Année de publication : |
2023 |
Article en page(s) : |
p. 637-653 |
Note générale : |
Bibliogr. |
Langues : |
Anglais (eng) |
Catégories : |
Agents dispersants (chimie) Dispersions et suspensions Dispersions et suspensions -- Stabilité Encre jet d'encre Ethoxylate d'alkyle MagentaLe magenta est un colorant rouge violacé d'aniline de synthèse inventé en 1858, appelé fuchsine ou roséine. C'est aussi la désignation normalisée du colorant primaire absorbant le vert dans la synthèse soustractive des couleurs en imprimerie et en photographie argentique. Masse molaireLa masse molaire est la masse d'une mole d'une substance (un corps simple, un composé chimique). Elle s'exprime en grammes par mole (g·mol−1 ou g/mol). Pigments -- Analyse Pigments organiques Polyacrylates QuinacridoneLes pigments de quinacridone sont des pigments organiques de synthèses qui vont du rouge-orange au rouge-violet.
Ils sont utilisés depuis les années 1960 par les teinturiers et les fabricants de pigment set couleurs à peindre (et plus récemment par certains tatoueurs, comme pigment dans des encres de tatouage, avec un risque allergique).
Il s'agit de pigments très transparents, au fort pouvoir colorant mais modérément couvrants.
Leur transparence permet de varier les teintes selon la densité et l'épaisseur de l'application. Terpolymère styrène anhydride maléïque
|
Index. décimale : |
667.2 Colorants et pigments |
Résumé : |
The stability of water-based pigment dispersions is a key factor in determining their utility in ink-jet applications, and the appropriate choice of dispersant plays a special role. Among the pigment formulations tested to date, literature data on magenta pigments are very limited. Thus, the goal of this work was to study the influence of the type and loading of dispersants on the quality and stability of quinacridone magenta pigment dispersions. Three different commercially available dispersants were tested: (1) a cationic styrene-maleic anhydride copolymer, (2) an anionic polyacrylate, and (3) a nonionic alkyl ethoxylate. Pigment and dispersing agents were analysed using the Fourier Transform–infrared method. The stability of pigment dispersions was determined by comparative studies of changes in the pigment particle size, viscosity, pH, filtration time, optical density and gloss during the accelerated ageing test. Moreover, Turbiscan AGS and LUMiFuge analysers were used for evaluations of the instability of the dispersions. The properties of each dispersing agent affected the performances of the different dispersants. The highest stability for the pigment formulations was provided using the nonionic dispersant (small particle size, < 60 nm; the lowest viscosity < 60 mPa·s at the optimal dispersant content; favourable results of the filtration test; the highest pigment dispersability, proven by optical density and gloss). The Turbiscan AGS and LUMiFuge results indicated that the stability of all tested quinacridone magenta pigment dispersions was excellent (Turbiscan Stability Index values below three, and no significant differences in transmission profiles, respectively). However, it was found that the measurement results were influenced by the viscosity of the formulations. |
Note de contenu : |
- EXPERIMENTAL : Materials - Equipment and measuring conditions - Methods
- RESULTS AND DISCUSSION : Analysis of the magenta pigment - Analysis of the dispersing agents - Stability study of pigment dispersions
- Table 1 : Dispersant type active matter content used in the prepared Magenta Pigment dispersions
- Table 2 : Molar mass of studied dispersants determined by gel permeation chromatography |
DOI : |
https://doi.org/10.1111/cote.12678 |
En ligne : |
https://onlinelibrary.wiley.com/doi/epdf/10.1111/cote.12678 |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40116 |
in COLORATION TECHNOLOGY > Vol. 139, N° 6 (12/2023) . - p. 637-653
[article]
|