Superior long-term performance of composite phase change material with high-density polyethylene under thermal aging process / Budhi Muliawan Suyitno in REVUE DES COMPOSITES ET DES MATERIAUX AVANCES, Vol. 33, N° 3 (06/2023)  

[article]  inREVUE DES COMPOSITES ET DES MATERIAUX AVANCES > Vol. 33, N° 3 (06/2023) . - p. 145-151 Titre : Superior long-term performance of composite phase change material with high-density polyethylene under thermal aging process Type de document : texte imprimé Auteurs : Budhi Muliawan Suyitno, Auteur ; Dwi Rahmalina, Auteur ; Ismail Ismail, Auteur ; Reza Abdu Rahman, Auteur Année de publication : 2023 Article en page(s) : p. 145-151 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Composites Polyéthylène haute densité Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Transition de phase En physique, une transition de phase est une transformation du système étudié provoquée par la variation d'un paramètre extérieur particulier (température, champ magnétique...). Cette transition a lieu lorsque le paramètre atteint une valeur seuil (plancher ou plafond selon le sens de variation). La transformation est un changement des propriétés du système. Index. décimale : 668.4 Plastiques, vinyles Résumé : Protecting the phase change material (PCM) from thermal aging is done by using polyethylene (high-density/HDPE) as supporting matrix. The HDPE content is set at 5 wt%, 10 wt% and 15 wt%. The composite PCM (cPCM) is treated through repeating melting/solidification process up to 10,000 cycles which is conducted between temperature 55℃-65℃. The thermal capacity of the paraffin wax (PW) is reduced notably, where enthalpy of fusion is decreased from 145.92 J/g to 138.46 J/g. The cPCM with 10 wt% and 15 wt% HDPE maintain a notable performance with only reduces slightly from 130.7 J/g to 129.7 J/g and 127.7 J/g to 127.2 J/g, respectively. The supercooling degree of PW increases around 1.64℃, which accelerates the cooling rate to 4.81℃/min. The HDPE in the cPCM maintain the physical behavior of PW, which minimizes the shrinkage effect during solidification. The highest heating rate is found at 2.29℃/min with minor decrement (0.06℃/min) for cPCM 15 wt% HDPE after treatment. The finding from this work can be used for fundamental basis to develop a high cycle PCM which able to operate at extended cycle with minor supercooling degree that is suitable for temperature sensitive operation. Note de contenu : - Sample detail and characterization - Cycling treatment - Heating/charging evaluation - Table 1 : Detailed sample for thermal treatment (percentage weight basis) DOI : https://doi.org/10.18280/rcma.330302 En ligne : https://www.iieta.org/download/file/fid/103796 Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=40023 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24247	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)