[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 5 (09/2023) . - p. 1513-1527 Titre : Effect of boron nitride modified by sodium tripolyphosphate on the corrosion resistance of waterborne epoxy coating Type de document : texte imprimé Auteurs : Hongrui Yao, Auteur ; Wenya Bi, Auteur ; Xu Yin, Auteur ; Shenglong Mu, Auteur ; Shiqiang Sha, Auteur ; Na Wang, Auteur Année de publication : 2023 Article en page(s) : p. 1513-1527 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosifs Anticorrosion Epoxydes Métaux -- Revêtements protecteurs Nitrure de bore Le nitrure de bore est un composé chimique du bore et de l'azote, de formule chimique brute BN (nombre égal d'atomes de chaque élément). Le nitrure de bore est isoélectronique avec le carbone et, comme ce dernier, existe sous plusieurs formes polymorphiques, dont l'une est analogue au diamant et l'autre au graphite. La forme diamant est l'un des matériaux les plus durs connus et la forme graphite est un lubrifiant apprécié. De plus, ces deux polymorphes possèdent des propriétés d'absorption radar. Revêtements en phase aqueuse Synergie Tripolyphosphate de sodium Index. décimale : 667.9 Revêtements et enduits Résumé : In this work, h-BN@STPP was successfully obtained by facile co-modification of sodium tripolyphosphate (STPP) and silane coupling agent (KH-550) on h-BN nanosheets, with waterborne epoxy coatings incorporated for metallic substrate corrosion protection. Results showed that the impedance modulus at the lowest frequency (Zf = 0.1 Hz) of h-BN@STPP composite coating increased three orders of magnitude in comparison with neat waterborne epoxy coating, exhibiting outstanding corrosion resistance. The reinforced anticorrosion performances of h-BN@STPP composite coatings could be attributed to the “labyrinth effect” of h-BN and passivation effect of STPP on the metal substrates. Note de contenu : - MATERIALS AND METHODS : Materials - Methods - Preparation of the composite coating modified by h-BN@STPP - Characterization - RESULTS AND DISCUSSION : Characterization of h-BN@STPP composite - Corrosion behavior of the composite coatings - Table 1 : Formulations of coatings - Table 2 : Impedance modulus at the lowest frequency (Zf = 0.1 Hz × 106 Ω·cm2) for different coatings immersed in 3.5 wt% NaCl solution for various time intervals DOI : https://doi.org/10.1007/s11998-023-00637-7 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00637-7.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39968 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24242	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)