Effect of polytetrafluoroethylene (PTFE) emulsion impregnation coating on filtration performance and thermal property of polyphenylene sulfide (PPS) needle felt / Chao Lv in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 4 (07/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 4 (07/2023) . - p. 1423-1433 Titre : Effect of polytetrafluoroethylene (PTFE) emulsion impregnation coating on filtration performance and thermal property of polyphenylene sulfide (PPS) needle felt Type de document : texte imprimé Auteurs : Chao Lv, Auteur ; Ruiqing Shen, Auteur ; Yang Yang, Auteur ; Rui Shu, Auteur ; Guodong Li, Auteur ; Jingxian Liu, Auteur Année de publication : 2023 Article en page(s) : p. 1423-1433 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Feutre (textiles et tissus) Filtration Matériaux -- Imprégnation Matériaux aiguilletés Polytétrafluoréthylène Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Revêtements -- Propriétés thermiques Revêtements en phase aqueuse Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : Polytetrafluoroethylene (PTFE) emulsion is widely used as a coating material in the impregnation process for preparing polyphenylene sulfide (PPS) needle felts due to its excellent chemical stability and good mechanical properties. However, the effect of emulsion impregnation coating on the filtration performance of needle felts is still under debate. Moreover, in industrial applications with high temperatures, the service life of needle felts is directly affected by their thermal stability, but the pyrolysis and kinetic properties of PPS needle felt after PTFE emulsion impregnation post-processing have rarely been quantitatively investigated. In this study, the PPS fiber/PTFE emulsion (PPS/PTFE) composite needle felt was fabricated by a direct impregnation process. The pressure drop characteristic and mechanical collection efficiency of PPS needle felt and PPS/PTFE composite needle felt were comprehensively evaluated. It was found that the PTFE emulsion impregnation coating not only increases the pressure drop, but also decreases the collection efficiency. More specifically, for particles having a size below 2.5 μm, the decrement of collection efficiency further increases with the decrease of particle size, but the mechanical collection efficiency of PPS/PTFE composite needle felt for particles having larger size is almost the same as that of PPS needle felt. Three emulsion impregnation coating distribution models were inferred to systematically explain this experimental phenomenon. Additionally, the thermal degradation process of PPS needle felt and PPS/PTFE composite needle felt was analyzed, and several typical pyrolysis kinetic parameters were also determined theoretically. It was confirmed that the PTFE emulsion impregnation coatings can enhance the thermal stability of PPS needle felts. This work provides new insight into the rational application of the direct impregnation process as well as emulsion impregnation coating in the industrial filtration field. Note de contenu : - MATERIALS AND METHODS : - Materials - Preparation of PPS/PTFE composite needle felt - Characterizations - RESULTS AND DISCUSSION : - Pressure drop characteristics and mechanical collection efficiency - Thermal degradation process and reaction kinetics - Table 1 : Information of experimental materials DOI : https://doi.org/10.1007/s11998-022-00755-2 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00755-2.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39726 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24153	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)