Comparison of viscoelastic behaviour in silica flled cured and uncured cpe/nr blends with various mixing time / Nilobon Phewthongin in APPLIED RHEOLOGY, Vol. 16, N° 4 (2006)

[article]  inAPPLIED RHEOLOGY > Vol. 16, N° 4 (2006) . - p. 182-189 Titre : Comparison of viscoelastic behaviour in silica flled cured and uncured cpe/nr blends with various mixing time Type de document : texte imprimé Auteurs : Nilobon Phewthongin, Auteur ; Pongdhorn Saeoui, Auteur ; Chakrit Sirisinha, Auteur Année de publication : 2006 Article en page(s) : p. 182-189 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caoutchouc Polyéthylène chloré Rhéologie Silice La silice est la forme naturelle du dioxyde de silicium (SiO2) qui entre dans la composition de nombreux minéraux. La silice existe à l'état libre sous différentes formes cristallines ou amorphes et à l'état combiné dans les silicates, les groupes SiO2 étant alors liés à d'autres atomes (Al : Aluminium, Fe : Fer, Mg : Magnésium, Ca : Calcium, Na : Sodium, K : Potassium...). Les silicates sont les constituants principaux du manteau et de l'écorce terrestre. La silice libre est également très abondante dans la nature, sous forme de quartz, de calcédoine et de terre de diatomée. La silice représente 60,6 % de la masse de la croûte terrestre continentale. Viscoélasticité Index. décimale : 532.05 Mécanique des fluides et des liquides - Dynamique (cinétique et cinématique) Résumé : Des mélanges de caoutchouc naturel (NR) avec du polyéthylène chloré (CPE) renforcé par de la silice 30-phr ont été préparés pour un ratio de composition de 80/20 CPE/NR en variant le temps de mélange entre 120 et 600 s. Les comportements viscoélastiques des mélanges réticulés et non réticulés ont été déterminés en utilisant deux rhéomètres avec deux modes de cisaillement, c-à-d, le rhéomètre oscillatoire (Rubber Process Analyser, RPA2000) et le rhéomètre capillaire à vitesse contrôlée (Goettfert Rheotester 2000). Les résultats obtenus révèlent que le comportement viscoélastique des mélanges est influencé par la formation d’un réseau transitoire de silice, particulièrement dans les mélanges réticulés. Le temps de mélange affecte significativement les propriétés viscoélastiques des mélanges vulcanisés, ce qui est probablement du au grand degré de dégradation thermique, tandis qu’il ne joue pas de rôle significatif pour les propriétés viscoélastiques des mélanges non vulcanisés. La superposition des résultats oscillatoires et de cisaillement en régime établi est possible quand la composante élastique est éliminée des résultats. DOI : 10.3933/ApplRheol-16-182 Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=26621 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
005644	-	Périodique	Bibliothèque principale	Documentaires	Disponible

Dispersion enhancement of multi-walled carbon nanotubes in nitrile rubber / A. Boonbumrung in INTERNATIONAL POLYMER PROCESSING, Vol. XXIX, N° 3 (07/2014)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXIX, N° 3 (07/2014) . - p. 317-324 Titre : Dispersion enhancement of multi-walled carbon nanotubes in nitrile rubber Type de document : texte imprimé Auteurs : A. Boonbumrung, Auteur ; P. Sae-oui, Auteur ; Chakrit Sirisinha, Auteur Année de publication : 2014 Article en page(s) : p. 317-324 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caoutchouc nitrile-butadiène Composites à fibres de carbone -- Propriétés électriques Composites à fibres de carbone -- Propriétés mécaniques Mélange Nanotubes Nanotubes de carbone à parois multiples Un nanotube de carbone multifeuillet est constitué de plusieurs feuillets de graphènes enroulés les uns autour des autres. Il existe deux modèles pour décrire la structure des nanotubes multifeuillets : - le modèle poupée russe: les plans de graphène sont arrangés en cylindres concentriques ; - le modèle parchemin: un seul feuillet de graphène est enroulé sur lui-même, comme une feuille de papier. Nitrique, Acide Permanganate de potassium Sulfurique, Acide Traitement chimique Ultrasons Index. décimale : 668.4 Plastiques, vinyles Résumé : A study of reinforcement mechanism of multi-walled carbon nanotubes (MWCNT) in nitrile rubber (NBR) matrix was carried out. Attempts to enhance the dispersion degree of MWCNT and the NBR-MWCNT interaction were conducted using numerous approaches, namely, sonication and chemical treatments of MWCNT with nitric acid (HNO3), nitric-sulfuric acid mixture (HNO3/H2SO4) and potassium permanganate (KMnO4). Rheological behavior, dynamic properties and electrical properties of MWCNT/NBR vulcanizates were monitored. Results gained reveal the magnitude of Payne effect increases with MWCNT content and mixing time. The expanded MWCNT and continuous-network formation are observed with an increase in mixing time, yielding enhanced mechanical properties and electrical properties. With MWCNT modification, a significant reduction in the state-of-mix of MWCNT composites is exhibited. SEM results demonstrate the highest magnitude of MWCNT dispersion in the system with HNO3, but relatively poor interaction with NBR. The HNO3/H2SO4 or KMnO4 system demonstrates poor MWCNT dispersion after treatment which is probably due to the compaction of MWCNT during the drying stage after the chemical treatment process, giving the detrimental effect to mechanical and electrical properties of vulcanizates. Note de contenu : - EXPERIMENTAL : Materials - Composite preparation - RESULTS AND DISCUSSION : Effect of mixing time - Effect of MWCNT modification DOI : 10.3139/217.2928 En ligne : https://drive.google.com/file/d/1GlLhu_VldQPbLjN1_w1EYZ7HuzVDyUJv/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=21728 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
16404	-	Périodique	Bibliothèque principale	Documentaires	Disponible

Rheological properties of chlorinated poyethylene blended with low-cost grade natural rubber / P. Wongwitthayakool in INTERNATIONAL POLYMER PROCESSING, Vol. XXIV, N° 1 (03/2009)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. XXIV, N° 1 (03/2009) . - p. 9-15 Titre : Rheological properties of chlorinated poyethylene blended with low-cost grade natural rubber Type de document : texte imprimé Auteurs : P. Wongwitthayakool, Auteur ; P. Saeoui, Auteur ; Chakrit Sirisinha, Auteur Année de publication : 2009 Article en page(s) : p. 9-15 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Alliages polymères Caoutchouc Polyéthylène Rhéologie Index. décimale : 668.9 Polymères Résumé : A low-cost grade natural rubber (STR20 NR) was used for partly substituting elastomeric chlorinated polyethylene (CPE) and then cured by sulfur. Rheological properties of blends with various blend composition ratios under oscillatory and steady shear flows were investigated. Cure behavior is found to be promoted with increasing NR content. The viscoelastic behavior of CPE/NR blends, as determined from the Rubber Process Analyzer (RPA2000), is controlled strongly by blend composition. Uncured blends show relatively poor storage modulus associated with high damping factor probably due to the thermal degradation of NR phase. By contrast, after curing the NR phase in blends, bulk rheological properties change remarkably. Blends with NR as a major component reveal frequency-independent behavior with a broad linear viscoelastic (LVE) region. Flow properties under capillary shear of uncured blends agree well with those under oscillatory shear, i.e., the greater the NR content, the lower the apparent shear viscosity. Surprisingly, even without the elimination of elastic effect by the Bagley correction, it is still possible to superimpose plots of complex viscosity against test frequency over those of apparent shear viscosity against wall shear rate, which are different from the rheological properties of CPE blended with premium grade of NR (STR5L). DOI : 10.3139/217.2081 En ligne : https://drive.google.com/file/d/1zqebevpOH9nvA6dEhjtcklZB6vql4dka/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=4202 [article]