Antistatic and antibacterial two-component waterborne polyurethane coating / Xianwen Li in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 3 (05/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 3 (05/2023) . - p. 869-881 Titre : Antistatic and antibacterial two-component waterborne polyurethane coating Type de document : texte imprimé Auteurs : Xianwen Li, Auteur ; Xinmeng Xu, Auteur ; Faai Zhang, Auteur Année de publication : 2023 Article en page(s) : p. 869-881 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Antibactériens Antistatiques Caractérisation Cuivre Nanoparticules Polyaniline Polyuréthanes Revêtements bi-composant Revêtements en phase aqueuse Revêtements organiques Zircone Le dioxyde de zirconium ou oxyde de zirconium(IV) couramment appelée zircone est un composé inorganique du zirconium de formule ZrO2. Ce matériau est une céramique technique d'aspect opaque. Appelé CZ (Cubic Zirconia) lorsque transparent, il est utilisé pour imiter le diamant. Il ne faut pas le confondre avec le zircon (ZrSiO4). Sous sa forme tétragonale, l'oxyde de zirconium est un matériau a vocation mécanique, cette évolution cristallographique lui confère une dureté très élevée (1200Hv) ainsi qu'une bonne résistance aux sollicitations mécaniques (700Mpa en traction et 2000Mpa en compression). Une fois polie, la zircone tétragonale peut atteindre un Ra de 0,02, ce qui permet de l'utiliser pour des pièces de frottement. Index. décimale : 667.9 Revêtements et enduits Résumé : Hydroxyl acrylate emulsion was prepared firstly by the semicontinuous seeded emulsion polymerization, and then adding polyaniline (PANI)/Cu/ZrO2 ternary nanocomposites, two-component waterborne polyurethane (2 K WPU) composite coatings with antistatic and antibacterial properties were obtained by mixing the emulsion with hydrophilic modified polyisocyanate. The structure and morphology of the PANI/Cu/ZrO2 were observed by Fourier transform infrared spectroscopy, scanning electron microscopy, and X-ray diffractometer. The thermal, antistatic, antibacterial, anticorrosion, and mechanical properties of the 2 K WPU composite coatings were determined. The results showed that the addition of the ternary nanocomposites increased the antistatic, antibacterial, anticorrosion, and mechanical properties of the 2 K WPU coating. The initial decomposition temperature increased from 200 to 225°C, and the tensile strength increased by 44.4%. The coatings still maintained good impact strength of 50/50 kg cm, adhesion of grade 2, flexibility of 1 mm, pendulum hardness of 293 s, and the gloss (60°) of 119.4. Note de contenu : - EXPERIMENTAL : Materials - Synthesis of PANI/Cu and PANI/Cu/ZrO 2 nanocomposites - Preparation of hydroxyl acrylate emulsion - Preparation of 2 K WPU film - Preparation of antibacterial and antistatic - 2 K WPU coatings - Preparation of culture medium - Characterization - Determination of surface electric resistance - Qualitative antibacterial test - Quantitatively antibacterial test - Coating anticorrosion resistance testing - Tinplate surface analysis - Adhesion, pendulum hardness, impact resistance, and gloss of films testing - Mechanical properties test - RESULTS AND DISCUSSION : FTIR - SEM images - XRD - Thermogravimetric analysis (TGA) - Antistatic property - Antibacterial property - Anticorrosion performance of the composite coatings - Coating performance of 2 K WPU composite - Table 1 : Effect of PANI/Cu/ZrO2 content on film performance of 2 K WPU DOI : https://doi.org/10.1007/s11998-022-00708-9 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00708-9.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39434 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24069	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)