[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 2 (03/2023) . - p. 457-468 Titre : Interaction of interfacial debonding and under-film corrosion propagation at the edge of the blistering area of epoxy coating Type de document : texte imprimé Auteurs : Chao Li, Auteur ; Jin Gao, Auteur ; Yunhua Huang, Auteur ; Xin Zhang, Auteur ; Xiaogang Li, Auteur Année de publication : 2023 Article en page(s) : p. 457-468 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Chimie des surfaces Cloquage (défauts) Corrosion Epoxydes Revêtements organiques Spectroscopie d'impédance électrochimique Index. décimale : 667.9 Revêtements et enduits Résumé : The blistering of epoxy coating and its evolution were investigated after being exposed to 3.5 wt% NaCl solution. The evolution of under-film corrosion could be divided into four stages according to the observation of the corrosion morphology and the distribution of corrosion products and elements. Corrosion propagation was related to the distribution of media at the edge of the blistering area. Local electrochemical impedance spectroscopy analysis revealed that local impedance mapping could help in predicting the direction of corrosion propagation. The interfacial debonding at the edge of the blistering area was a necessary condition for corrosion propagation. Note de contenu : - EXPERIMENT : Specimens - Instrumentation - RESULTS : Analysis of microenvironment under blistering - Local electrochemical impedance of the blistering area DOI : https://doi.org/10.1007/s11998-022-00680-4 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00680-4.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39291 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
24056	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)