Separation of a nanofiller from tannery effluents / Anita Przepiórkowska in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC), Vol. 90, N° 1 (01-02/2006)  

[article]  inJOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 90, N° 1 (01-02/2006) . - p. 7-9 Titre : Separation of a nanofiller from tannery effluents Type de document : texte imprimé Auteurs : Anita Przepiórkowska, Auteur ; M. Prochon, Auteur ; K. Chronska, Auteur ; M. Zaborski, Auteur Année de publication : 2006 Article en page(s) : p. 7-9 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Alliages polymères Caoutchouc nitrile-butadiène Charges (matériaux) Chaulage Craie La craie est une roche sédimentaire calcaire blanche marine de type biomicrite, de texture mudstone à packstone, à grain généralement très fin, tendre, marquante, poreuse et perméable, et assez pure contenant presque exclusivement du carbonate de calcium CaCO3 (90 % ou plus) et un peu d'argile. Formée dans des mers chaudes et peu profondes, elle est constituée essentiellement1 par l'accumulation d'algues planctoniques (surtout des coccolithes), auxquelles s’ajoutent en quantité variable des fragments d'inocérames, d'échinodermes ou de bryozoaires, ainsi que des foraminifères2. Les principales accumulations de craie en Europe datent du Crétacé, période géologique à laquelle la craie a donné son nom. La craie est un calcaire souvent très pur, elle peut cependant être marneuse (lorsque le taux d'argile atteint des proportions plus élevées), glauconieuse (si elle contient de la glauconie), dolomitique (si elle contient des recristallisations de dolomite comme dans la craie de Vernon), à silex, etc. La craie contient fréquemment des niveaux de silex interstratifiés. Le tuffeau est de la craie micacée ou sableuse à grain fin, de couleur blanche ou crème parfois jaunâtre, contenant quelques paillettes de mica blanc (muscovite). Cuirs et peaux -- Déchets Eaux usées -- Epuration Nanoparticules Séparation (technologie) Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : Recent years have witnessed a growing interest in the technology of nano-materials. Numerous studies have been carried out on the synthesis and modification of nanometersized polymeric materials based on nanofillers. Meanwhile, tannery plants are faced with a serious problem of the utilization of effluents from the processes of leather dressing. The most serious problem is the wastewater from so-called beamhouse or the operations of soaking, depilation and liming. Despite the implementation of technology with reduced water consumption, the effluents still amount to about 80% of wastewater from all the manufacturing processes.1 Most tanneries use the liming process to unhair hides by destroying the hair structure. The process has a low chemicals cost, good reproducibility of results and easy control of the process. 2. The effluents from the liming process contain two groups of impurities : Organic pollutants, mainly products of degradation of non-collagen proteins, proteins of hair, bristle and epidermis as well as fatty substances. Inorganic impurities, mainly lime and calcium compounds, residual chlorides from preservation, sodium sulfide and sulfates. Note de contenu : - EXPERIMENTAL METHODS : Use as rubber filler - DISCUSSION OF TEST RESULTS : IR spectroscopy of the precipitate - Zeta potentials of aqueous dispersions of the tested precipitate and precipitated chalk - Specific surface of the precipitate - Measurement of particle size - Properties of mixes and vulcanisates/rubber - Table 1 : Properties of mixes and vulcanizates of butadiene-acrylonitrile rubber (NBR) - Table 2 : Properties of mixes and vulcanizates of carboxylated butadieneacrylonitrile rubber (XNBR) En ligne : https://drive.google.com/file/d/18Mec7IrU9cr9fGTY_Lk0aN8QDgA27_aM/view?usp=share [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=39177 [article]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

---

1 (1 - 1 / 1)