One-step synthesis of epoxy-based silicon prepolymers and its application in UV-curable coating / Fuping Bian in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 1 (01/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 1 (01/2023) . - p. 321-331 Titre : One-step synthesis of epoxy-based silicon prepolymers and its application in UV-curable coating Type de document : texte imprimé Auteurs : Fuping Bian, Auteur ; Xiaoquan Li, Auteur ; Jihe Zhao, Auteur ; Jiwen Hu, Auteur ; Xuefeng Gui, Auteur ; Shi Li, Auteur ; Shudong Lin, Auteur Année de publication : 2023 Article en page(s) : p. 321-331 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosion Caractérisation Composés organiques -- Synthèse Epoxydes Essai Wolff-Wilborn Hydrophobie Hydrosilylation La réaction d'hydrosilylation consiste en l'addition d'une fonction hydrogénosilane (Si-H) sur un composé organique insaturé. Il existe principalement deux méthodes pour mettre en Å“uvre cette réaction : La génération de radicaux silyle : thermiquement (300 °C), par irradiation (rayonnement ultraviolet ou par décomposition de peroxydes ou d'azonitriles. La catalyse par des métaux de transition généralement du groupe VIII. Parmi ces différents catalyseurs employés pour la réaction d'hydrosilylation, les composés à base de platine et plus particulièrement l'acide hexachloroplatinique hexahydraté sont ceux qui présentent la plus grande efficacité1. Ce catalyseur utilisé en très faible quantité et pour des temps de réaction généralement inférieurs à 5 h permet d'atteindre des rendements relativement élevés. Un mécanisme plus récent de l'hydrosilylation a été proposé dans la thèse de Patrick Cancouët sur un polysiloxane porteur de fonction hydrogénosilanes latérales. Oligomères Polyaddition Prépolymères Un pré-polymère ou prépolymère est un oligomère ou un polymère présentant des groupes réactifs qui lui permettent de participer à une polymérisation ultérieure et d’incorporer ainsi plusieurs unités monomères dans au moins une chaîne de la macromolécule finale. Les pré-polymères peuvent être di-fonctionnels (c'est le cas des pré-polymères téléchéliques) ou plurifonctionnels. Dans ce dernier cas, ils sont utilisés pour la fabrication de polymères thermodurcissables par réticulation. Résistance aux taches Résistance chimique Revêtements -- Propriétés thermiques Revêtements organiques Silicones Les silicones, ou polysiloxanes, sont des composés inorganiques formés d'une chaine silicium-oxygène (...-Si-O-Si-O-Si-O-...) sur laquelle des groupes se fixent, sur les atomes de silicium. Certains groupes organiques peuvent être utilisés pour relier entre elles plusieurs de ces chaines (...-Si-O-...). Le type le plus courant est le poly(diméthylsiloxane) linéaire ou PDMS. Le second groupe en importance de matériaux en silicone est celui des résines de silicone, formées par des oligosiloxanes ramifiés ou en forme de cage (wiki). Transparence (optique) Index. décimale : 667.9 Revêtements et enduits Résumé : As described herein, a simple one-step hydrosilylation reaction was employed to synthesize alicyclic epoxy silicone prepolymers by using poly(dimethylsiloxane-co-methylhydrosiloxane) (PDMS-PHMS) with different hydrogen contents and 4-vinyl-1-cyclohexene-1,2 epoxide (VCHO) as precursors. The structures of the synthesized epoxy polysiloxane oligomer was characterized by Fourier-transform infrared (FTIR) and proton nuclear magnetic resonance (1H-NMR) spectroscopy techniques, thus confirming the successful synthesis of the prepolymers. With the addition of an appropriate amount of cationic photoinitiator, the epoxy polysiloxane prepolymers undergo cationic polymerization under ultraviolet light irradiation and were quickly cured to yield series of epoxy polysiloxane resin films. The performances of these cured films were tested and characterized by various techniques such as UV transmittance, thermal weight loss analysis, and contact angle and pencil hardness measurements. The results revealed that the surfaces of these films were uniform and transparent, and these films had excellent heat resistance, acid resistance, hydrophobicity, and ink removal properties. In addition, the influence of the cycloaliphatic epoxy monomer content on the curing behavior and network performance is explored. This study reveals that the curing rate increases as the amount of grafted cycloaliphatic epoxy monomer is increased and that a denser crosslinking network provides the resultant film. Finally, the photocurable silicone material investigated herein is simple to prepare and has excellent performance, and has potential applications in the field of anti-smudge coatings. Note de contenu : - EXPERIMENTAL : Materials - Synthesis of the prepolymers - Preparation of the UV-curable films - Characterization - RESULTS AND DISCUSSION : FTIR spectroscopy and 1H-NMR characterization - GPC analysis - UV curing process - Transparency - TGA - Hydrophobicity - Anti-smudge performance - Corrosion - Resistance exposure to hydrochloric acid - Pencil hardness test - Table 1 : Information regarding the PDMS-PHMS - Table 2 : The GPC results of PDMS-PHMS-C and prepolymer C - Table 3 : Prepolymer A swelling ratio and gel fraction - Table 4 : Thermal properties of the UV-cured coatings - Table 5 : Corrosion resistance exposure to hydrochloric acid - Table 6 : Pencil hardness test of three kinds of prepolymer light-cured films DOI : https://doi.org/10.1007/s11998-022-672-4 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00672-4.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38845 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23928	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)