Design and fabrication of superhydrophobic layered double hydroxide and oxides composite coating on brass mesh with excellent anticorrosion, delay icing and oil-water separation ability / Yuanyuan Wang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 20, N° 1 (01/2023)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 20, N° 1 (01/2023) . - p. 275-289 Titre : Design and fabrication of superhydrophobic layered double hydroxide and oxides composite coating on brass mesh with excellent anticorrosion, delay icing and oil-water separation ability Type de document : texte imprimé Auteurs : Yuanyuan Wang, Auteur ; Qian Zhong, Auteur ; Linqiu Wu, Auteur ; Pengfei Liu, Auteur ; Hangmin Guan, Auteur ; Yingfei Hu, Auteur ; Qing Lin, Auteur ; Wei Wang, Auteur Année de publication : 2023 Article en page(s) : p. 275-289 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosifs Anticorrosion Caractérisation Composites Filtres auto-nettoyants Hydroxydes doubles lamellaires Laiton Les laitons sont des alliages jaunes, très ductiles et malléables, composés essentiellement de cuivre et de zinc, aux proportions variables, dont la fabrication directe à partir de minerais appropriés était déjà maîtrisée par les métallurgistes avant l'Antiquité. Selon les propriétés visées, ils peuvent aujourd'hui contenir d'autres éléments d'addition comme le plomb, l'étain, le nickel, le chrome et le magnésium, dans des proportions très modérées. (Wikipedia) Maille métallique Oléophilie Revêtements Revêtements antigel Séparation huile/eau Index. décimale : 667.9 Revêtements et enduits Résumé : In this work, a superhydrophobic and superoleophilic brass mesh had been prepared. The prepared sample displayed a water contact angle (WCA) of 160o and was characterized by field emission scanning electron microscope (FE-SEM), white light interferometer (WLI), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) techniques. Besides, a high-speed camera was used to study the impact process of a droplet on the surface of the prepared sample. The superhydrophobic brass mesh exhibited excellent self-cleaning ability, environmental adaptability, corrosion resistance (η = 98.9%), and delayed icing ability (~ 45 min). Furthermore, the superhydrophobic mesh could be used as a filter to fast and efficiently separate various kinds of oils (light and heavy oils) and oil pollutants in daily life and industry. The superhydrophobic filter could be reused 50 times for oil-water separation without any apparent decrease in its separation capability. Thus, the superhydrophobic brass mesh prepared by a simple method holds promise for various applications in the industrial field of oil-water separation. Note de contenu : EXPERIMENTAL AND CHARACTERIZATION : Materials - Sample preparation - Sample characterizations - Self-cleaning ability - Environmental adaptability - Corrosion resistance - Delayed icing test - Oil-water separation - RESULTS AND DISCUSSION : Surface morphology, roughness and composition - Surface wettability - Self-cleaning ability - Environmental adaptability - Corrosion resistance - Delayed icing ability - Oil-water separation - Table 1: Corrosion potential, corrosion current, and corrosion resistance efficiency of the original brass mesh, Brass-LDH, and Brass-LDH-SA in a 3.5 wt% NaCl solution DOI : https://doi.org/10.1007/s11998-022-00667-1 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00667-1.pdf?pdf=button% [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38842 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23928	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)