Anticorrosion properties of modified basalt powder/epoxy resin coating / Manxia Zhang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 5 (09/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 5 (09/2022) . - p. 1409-1420 Titre : Anticorrosion properties of modified basalt powder/epoxy resin coating Type de document : texte imprimé Auteurs : Manxia Zhang, Auteur ; Xinyi Zhao, Auteur ; Hang Jia, Auteur ; Haoran Xing, Auteur ; Hongjing Zhang, Auteur ; Xinyue Wang, Auteur ; Cheng Liu, Auteur Année de publication : 2022 Article en page(s) : p. 1409-1420 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosifs Anticorrosion Basalte Caractérisation Enrobage (technologie) Epoxydes Mesure Poudres Réaction de couplage Revêtements -- Propriétés mécaniques Revêtements organiques Spectroscopie d'impédance électrochimique Traîtements de surface Index. décimale : 667.9 Revêtements et enduits Résumé : The epoxy resin coating has been widely used; however, its anticorrosion performance still needs to be improved. Basalt materials have been used as fillers in the field of anticorrosive coatings due to their good corrosion resistance and acid and alkali resistance. In this paper, 3-aminopropyltrimethoxysilane (APTMS) was used as a coupling agent to modify the surface of basalt powder. The modified basalt powder (MBP) was characterized by scanning electron microscope (SEM) and Fourier transform infrared-attenuated total reflectance (FTIR-ATR). The MBP was added to epoxy resin in different proportions as fillers, and the coatings with different MBP contents were prepared by applying the mixture on the metal substrates. The hardness of coatings can be enhanced up to 0.25 GPa with the increase in MBP, and the elastic of coatings increases to the highest of 4.97 GPa for MBP-10/EP. Their water absorption rates after soaking in water for 21 h decreased to 0.75%. Meanwhile, the anticorrosion performance of the coatings on substrates during exposure to 3.5 wt% NaCl solution was investigated by using electrochemical impedance spectroscopy (EIS), and the circuit-fitting of EIS tests was also performed. The corrosion resistance of EP coating has been obviously improved by adding MBP, with the low-frequency impedance value (|Z|0.01Hz) of MBP-10/EP up to 2.43 × 108 Ω·cm2 after being immersed in 3.5 wt% NaCl solution for 15 d, which was 7.8 times higher than that of neat epoxy coating (MBP-0/EP). Note de contenu : - EXPERIMENTAL : Materials - Sample preparation - Measurement and characterization - RESULTS AND DISCUSSION : Characterization of BP and MBP - Characterization of coatings - Table 1 : Chemical composition analysis of basalt powder - Table 2 : Mechanical properties of MBP/EP coatings - Table 3 : Corrosion voltage and corrosion current density of the coatings immersed in 3.5 wt% NaCl solution for 15 d - Table 4 : Changes of electrochemical fitting parameters of each coating immersed in 3.5 wt% NaCl solution for 15 d DOI : https://doi.org/10.1007/s11998-022-00615-z En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-00615-z.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38279 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23672	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)