Corrosion resistance of functionalized carbon nanotubes enhanced epoxy coatings on sintered NdFeB magnets / Hongyi yang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 5 (09/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 5 (09/2022) . - p. 1317-1329 Titre : Corrosion resistance of functionalized carbon nanotubes enhanced epoxy coatings on sintered NdFeB magnets Type de document : texte imprimé Auteurs : Hongyi yang, Auteur ; Liangsong Duan, Auteur ; Pengjie Zhang, Auteur ; Guangqing Xu, Auteur ; Jiewu Cui, Auteur ; Jun Lv, Auteur ; Wei Sun, Auteur ; Bingshan Li, Auteur ; Dongmei Wang, Auteur ; Yucheng Wu, Auteur Année de publication : 2022 Article en page(s) : p. 1317-1329 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosifs Anticorrosion Caractérisation Composites à fibres de carbone Epoxydes Essais de résilience Matériaux -- Propriétés fonctionnelles Nanotubes de carbone à parois multiples Un nanotube de carbone multifeuillet est constitué de plusieurs feuillets de graphènes enroulés les uns autour des autres. Il existe deux modèles pour décrire la structure des nanotubes multifeuillets : - le modèle poupée russe: les plans de graphène sont arrangés en cylindres concentriques ; - le modèle parchemin: un seul feuillet de graphène est enroulé sur lui-même, comme une feuille de papier. Revêtements organiques Surfaces fonctionnelles Tanins Index. décimale : 667.9 Revêtements et enduits Résumé : In this work, tannic acid (TA) was employed to modify the surface of multiwall carbon nanotubes (CNTs) to form TCNTs hybrids via noncovalent functionalization to enhance its dispersibility in water. Then, the TCNTs enhanced epoxy coatings were applied on sintered NdFeB magnets by cathodic electrophoretic deposition method for corrosion test. The corrosion resistance of prepared specimens was assessed by electrochemical experiments. The results show that TCNTs hybrids present a more homogeneous distribution in epoxy resin than pristine CNTs and could obviously promote anticorrosion properties of prepared specimens. Within 36-day soaking in 3.5 wt.% NaCl solution, the specimens maintain a high value of |Z|0.01Hz (108 Ω cm2) when the concentration of TCNTs is 2 g/L. When immersed in 3.5 wt.% NaCl solution for 40 days, the Ecorr of specimens shifts to − 0.207 V and Jcorr is about 5.281 × 10−11 A cm−2, which demonstrates superior corrosion resistance. Note de contenu : - EXPERIMENT : Materials - Experimental method - Material characterization and corrosion resistance test - RESULTS AND DISCUSSION : Characterization of TCNTs hybrids - Characterization of specimens - Corrosion protection mechanism - Table 1 : Surface chemical composition of CNTs and TCNTs hybrids - Table 2 : |Z|0.01Hz of specimens after being immersed in 3.5 wt.% NaCl solution for different times - Table 3 : Electrochemical polarization parameters of different specimens - Table 4 : Comparation of corrosion protection data of chemical oxidized CNTs enhanced epoxy coatings with this work DOI : https://doi.org/10.1007/s11998-022-00641-x En ligne : https://link.springer.com/content/pdf/10.1007/s11998-022-006241-x.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38272 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23672	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)