Preparation and characterization of hydrogen-containing silicone oil-modified polyurethane/Al composite coating with low-infrared emissivity / Weigang Zhang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 3 (05/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 3 (05/2022) . - p. 897-905 Titre : Preparation and characterization of hydrogen-containing silicone oil-modified polyurethane/Al composite coating with low-infrared emissivity Type de document : texte imprimé Auteurs : Weigang Zhang, Auteur ; Si Xiong, Auteur ; Dandan Lv, Auteur Année de publication : 2022 Article en page(s) : p. 897-905 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Aluminium L'aluminium est un élément chimique, de symbole Al et de numéro atomique 13. C’est un métal pauvre, malléable, de couleur argent, qui est remarquable pour sa résistance à l’oxydation13 et sa faible densité. C'est le métal le plus abondant de l'écorce terrestre et le troisième élément le plus abondant après l'oxygène et le silicium ; il représente en moyenne 8 % de la masse des matériaux de la surface solide de notre planète. L'aluminium est trop réactif pour exister à l'état natif dans le milieu naturel : on le trouve au contraire sous forme combinée dans plus de 270 minéraux différents, son minerai principal étant la bauxite, où il est présent sous forme d’oxyde hydraté dont on extrait l’alumine. Il peut aussi être extrait de la néphéline, de la leucite, de la sillimanite, de l'andalousite et de la muscovite. L'aluminium métallique est très oxydable, mais est immédiatement passivé par une fine couche d'alumine Al2O3 imperméable de quelques micromètres d'épaisseur qui protège la masse métallique de la corrosion. On parle de protection cinétique, par opposition à une protection thermodynamique, car l’aluminium reste en tout état de cause très sensible à l'oxydation. Cette résistance à la corrosion et sa remarquable légèreté en ont fait un matériau très utilisé industriellement. L'aluminium est un produit industriel important, sous forme pure ou alliée, notamment dans l'aéronautique, les transports et la construction. Sa nature réactive en fait également un catalyseur et un additif dans l'industrie chimique ; il est ainsi utilisé pour accroître la puissance explosive du nitrate d'ammonium. Caractérisation Dioxyde de silicium Emissivité En transfert radiatif, l'émissivité correspond au flux radiatif du rayonnement thermique émis par un élément de surface à température donnée, rapporté à la valeur de référence qu’est le flux émis par un corps noir à cette même température. Cette dernière valeur étant la valeur maximale possible, l'émissivité est un nombre inférieur ou égal à l'unité. (widipedia) Hydrophobie Nanoparticules Polyuréthanes Poudres métalliques Rayonnement infrarouge Revêtement auto-nettoyant Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : The goal of this research was to obtain a coating with low-infrared emissivity and both good hydrophobic and mechanical properties. Using nano-SiO2 as the micro-nano structural modifier, a hydrogen-containing silicone oil (HCSO)-modified polyurethane (PU)/Al composite coating with super-hydrophobicity and low-infrared emissivity was prepared via a simple glass rod scraping method. Effects of the ratio of HCSO to PU, the total filler addition, and the ratio of Al powder and nano-SiO2 on the coating properties are systematically discussed. The results show that as the ratio of HCSO to PU increases, the surface energy of the coating decreases, and this significantly increases the hydrophobicity of the coating. When the ratio is 2:8, the coating has outstanding hydrophobic properties, the adhesion strength of the coating reaches grade 1, and the water contact angle (WCA) reaches 152°. The total filler addition has a significant impact on the coating performance. With an increase in the filler addition, the emissivity of the coating increases, and the glossiness decreases. When the total filler addition is 50 wt%, the coating surface forms an obvious papillary micro-nano rough structure, so that the coating has outstanding hydrophobic properties. The ratio of Al powder to nano-SiO2 obviously affects the emissivity and hydrophobic properties of the coating. When the ratio is 5.5:4.5, the coating has good overall performance. At this point, the emissivity of the coating is as low as 0.675; the glossiness and adhesion strength are 2.7 and grade 1, respectively; the WCA and sliding angle are 155° and 8°, respectively; and it has outstanding self-cleaning performance. Through the research in this paper, a low-infrared emissivity coating with outstanding super-hydrophobic properties and adhesion strength has been obtained and has important application value in the design and transformation of infrared stealth of various equipment. Note de contenu : - EXPERIMENTAL : Materials - Preparation of HCSO-modified PU/Al composite coating - Characterization - RESULTS AND DISCUSSION : Effects of ratio of HCSO to PU on coating performance - Effects of total filler addition on coating performance - Effects of ratio of Al powder to nano-SiO 2 on coating performance - Table 1 : Performance indicators of the coatings with different ratios of HCSO to PU - Table 2 : Performance indicators of the coatings with different amounts of fillers - Table 3 : Performance indicators of the coatings with different ratios of Al powder to nano-SiO2 DOI : https://doi.org/10.1007/s11998-021-00567-w En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00567-w.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38084 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23605	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)