Siloxane coating with epoxy modification : optimization of adhesion to improve steel corrosion protection / M. Barletta in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 3 (05/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 3 (05/2022) . - p. 839-849 Titre : Siloxane coating with epoxy modification : optimization of adhesion to improve steel corrosion protection Type de document : texte imprimé Auteurs : M. Barletta, Auteur ; P. Moretti, Auteur ; E. Pizzi, Auteur ; F. Trovalusci, Auteur Année de publication : 2022 Article en page(s) : p. 839-849 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Caractérisation Epaisseur -- Mesure Epoxydes Matériaux hybrides Métaux -- Revêtements protecteurs Procédés de fabrication Revêtements organiques Rugosité Silicones Les silicones, ou polysiloxanes, sont des composés inorganiques formés d'une chaine silicium-oxygène (...-Si-O-Si-O-Si-O-...) sur laquelle des groupes se fixent, sur les atomes de silicium. Certains groupes organiques peuvent être utilisés pour relier entre elles plusieurs de ces chaines (...-Si-O-...). Le type le plus courant est le poly(diméthylsiloxane) linéaire ou PDMS. Le second groupe en importance de matériaux en silicone est celui des résines de silicone, formées par des oligosiloxanes ramifiés ou en forme de cage (wiki). Index. décimale : 667.9 Revêtements et enduits Résumé : This study focuses on the possibility of using siloxane resins with epoxy modification to delay corrosion of metal substrates for hydraulic applications. Formulations aimed at metal protection were designed, without including anticorrosive additives, and deposited on 11SMnPb37 steel. Thin monolayer films were obtained by dip coating in different process conditions, avoiding primers. The developed procedure was simple and able to provide solid and well-anchored coatings. They were characterized in terms of morphology, scratch and wear endurance, and resistance to a corrosive environment. The optimum formulation and deposition parameters were found. The selected coating showed remarkable adhesion to the substrate, good mechanical properties, and resistance in a saline environment, proving to be suitable as a protective barrier against corrosion. The protective effect was ensured not by additives but through the excellent adhesion of the coating and its endurance to scratch and wear. Note de contenu : - Materials and manufacturing process - Characterization procedure - Table 1 : Coatings developed in the experiments - Table 2 : Mean thickness values of the coatings obtained in various conditions according to Table 1 (alkaline pretreatment of the support or absence, resin concentration, extraction speed) - Table 3 : Measured roughness (Ra and Rz) of uncoated sample and selected coatings, AC3S10, AC3S100, C3S10, and C3S100 DOI : https://doi.org/10.1007/s11998-021-00594-7 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00594-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38079 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23605	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)