Fabricating superhydrophobic surfaces via coating amine-containing fluorinated emulsion and Michael addition reaction / Jiajia Yuan in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 4 (07/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 4 (07/2022) . - p. 1187-1198 Titre : Fabricating superhydrophobic surfaces via coating amine-containing fluorinated emulsion and Michael addition reaction Type de document : texte imprimé Auteurs : Jiajia Yuan, Auteur ; Xue Yin, Auteur ; Zelin Qiu, Auteur ; Yujie Shen, Auteur ; Lifeng Fang, Auteur ; Zhiying Liang, Auteur ; Qingran Kong, Auteur ; Baoku Zhu, Auteur Année de publication : 2022 Article en page(s) : p. 1187-1198 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Amines Une amine est un composé organique dérivé de l'ammoniac dont certains hydrogènes ont été remplacés par un groupement carboné. Si l'un des carbones liés à l'atome d'azote fait partie d'un groupement carbonyle, la molécule appartient à la famille des amides. Découvertes en 1849, par Wurtz les amines furent initialement appelées alcaloïdes artificiels. On parle d'amine primaire, secondaire ou tertiaire selon que l'on a un, deux ou trois hydrogènes substitués. Par exemple, la triméthylamine est une amine tertiaire, de formule N(CH3)3. Typiquement, les amines sont obtenues par alkylation d'amines de rang inférieur. En alkylant l'ammoniac, on obtient des amines primaires, qui peuvent être alkylées en amines secondaires puis amines tertiaires. L'alkylation de ces dernières permet d'obtenir des sels d'ammonium quaternaire. D'autre méthodes existent : 1. Les amines primaires peuvent être obtenues par réduction d'un groupement azoture, 2. Les amines peuvent aussi être obtenues par la réduction d'un amide, à l'aide d'un hydrure, 3. L'amination réductrice permet l'obtention d'amines substituées à partir de composés carbonylés (aldéhydes ou cétones), 4. Les amines primaires peuvent être obtenues par la réaction de Gabriel. Caractérisation Fluor Hydrophobie Michael, Addition de L'addition de Michael ou réaction de Michael est une réaction qui permet la création de liaisons carbone-carbone, voire de liaisons carbone-soufre. Il s'agit de l'addition nucléophile d'un carbanion sur un composé carbonylé α,β insaturé (aldéhyde, cétone et même ester α,β insaturé, des nitriles et des amides α,β insaturés pouvant aussi être utilisés). Elle appartient à la famille des additions nucléophiles conjuguées. Cette réaction doit son nom au chimiste américain Arthur Michael. Polyacrylates Revêtements en phase aqueuse Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : In this work, highly fluorinated acrylate emulsions with reliable stability emulsified by protonated octadecylamine were successfully synthesized. With appropriate protonation, the obtained emulsion showed high monomer conversions up to 90.2% and ultralow surface energy. The ultralow-surface-energy coatings were fabricated via surface enrichment of abundant fluorine and replacing hydrophilic amino groups with hydrophobic groups through the Michael addition reaction. Superhydrophobic and self-cleaning surfaces were prepared on porous substrates through dip coating. When fabricated on porous glass fiber nonwoven mats, surfaces coated with enriching fluorinated side chains and few hydrophilic groups showed remarkable superhydrophobicity with a water contact angle more than 150º and a low sliding contact angle of 4.7°. The usage of fluorinated emulsions was sharply reduced due to the addition of perfluorinated acrylate. Moreover, the Michael acceptors were alternative such as perfluorinaed acrylates, long aliphatic acrylates and crosslinking acrylates, displaying superior hydrophobicity and waterproof properties. All the results conclusively indicated that this practical modified method was promising for potential applications of hydrophobic modifications. Note de contenu : - EXPERIMENTAL : Materials - Synthesis of the fluorinated acrylate emulsions - Finishing the fiber - Emulsion characterization - Surface properties - RESULTS AND DISCUSSION : Emulsion characterization - The Michael addition - Hydrophobic comparison - Hydrophobic performance - Analysis of chemical compositions - Other Michael acceptors - Table 1 : Summary of superhydrophobic coatings, finishing on fiber surface and fluorinated acrylic resin emulsions - Table 2 : Chemical and physical properties of synthesized samples - Table 3 : Contact angles and surface energy of synthesized samples - Table 4 : Surface chemical composition of the glass fibers before and after coating DOI : https://doi.org/10.1007/s11998-021-00600-y En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00600-y.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38046 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23574	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)