Titre : |
A study on the preparation of passivating surface using bi-layer of nanostructured ZnO and silane functionalized polymer: an alternate option to chromate passivating coating |
Type de document : |
texte imprimé |
Auteurs : |
Ashok Kumar Gupta, Auteur ; Surayakanta Nayak, Auteur ; Rakesh S. Moirangthem, Auteur ; T. Venugopalan, Auteur ; A. N. Bhagat, Auteur ; Tapan Kumar Rout, Auteur |
Année de publication : |
2022 |
Article en page(s) : |
p. 1101-1115 |
Note générale : |
Bibliogr. |
Langues : |
Américain (ame) |
Catégories : |
Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique.
L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1.
C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Caractérisation Corrosion Hydrophobie Métaux -- Revêtements protecteurs Nanostructures Oxyde de zinc Passivité (Chimie) PolydiméthylsiloxaneLe polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones.
Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone.
Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK).
La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Revêtements organiques Silanes
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
A novel bilayer coating was developed over flat steel surface using a simple solution dipping method. Zinc oxide nanostructure (ZnO-NS) on the surfaces of flat steel was grown by chemical treatment with zinc nitrate hexahydrate [Zn(NO3)·6H2O] and hexamethylenetetramine (HMTA, C6H12N4) in aqueous solution, followed by a thin-layer deposition of amine-terminated poly-dimethylsiloxane (PDMS-NH2). We noticed surface passivation, surface hydrophobicity, and anti-corrosion properties by this robust bilayer concept where both chemical and physical effects were present. The surface properties were measured by contact angle and scanning electron microscope. This nanostructured grown mild steel, i.e., cold-rolled closed annealed steel, was compared with nanostructure grown over zinc-coated steel, i.e., galvannealed and galvanized iron. Different flat-coated specimens were characterized by Fourier transform infrared spectroscopy. The formation of ZnO-NS on steel substrate was confirmed by XRD analysis. The corrosion behavior of the different specimens was also studied through DC polarization and electrochemical impedance spectroscopy. An excellent intact bilayer coating was proposed in the interest of structural and automotive applications. |
Note de contenu : |
- EXPERIMENTAL SECTION : Materials used - Preparation of ZnO-NS on steel surfaces (GA, GI, and CRCA) - Coating solution preparation - Coated sample/specimen preparation
- CHARACTERIZATION
- RESULTS AND DISCUSSION : Scanning electron microscopy (SEM) study - X-ray diffraction analysis - Fourier transform infrared (FTIR) spectroscopy - Contact angle measurement - Electrochemical impedance spectroscopy (EIS) study - Polarization study
- Table 1 : Details about substrates used for the preparation of different specimens
- Table 2 : EDS elemental composition of different coated samples
- Table 3 : EIS parameters of coated steel substrates during test under 3.5% NaCl solution
- Table 4 : Electrochemical data for different samples in 3.5% NaCl solution by DC polarization fittings |
DOI : |
https://doi.org/10.1007/s11998-021-00588-5 |
En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-021-00588-5.pdf |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38039 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 4 (07/2022) . - p. 1101-1115
[article]
|