Preparation and characterization of cationic waterborne polyurethanes containing a star-branched polydimethylsiloxane / Xiaoling He in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 4 (07/2022)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 4 (07/2022) . - p. 1055-1066 Titre : Preparation and characterization of cationic waterborne polyurethanes containing a star-branched polydimethylsiloxane Type de document : texte imprimé Auteurs : Xiaoling He, Auteur ; Jingwei He, Auteur ; Yangkun Sun, Auteur ; Xiaopei Zhou, Auteur ; Jingying Zhang, Auteur ; Fang Liu, Auteur Année de publication : 2022 Article en page(s) : p. 1055-1066 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Dépôt électrolytique Polydiméthylsiloxane Le polydiméthylsiloxane —[O-Si(CH3)2]n—, ou poly(diméthylsiloxane) selon la nomenclature systématique, communément appelé PDMS ou diméthicone, est un polymère organominéral de la famille des siloxanes souvent présent dans les shampoings. On l'y ajoute pour augmenter le volume des cheveux mais il peut également aller boucher les pores du cuir chevelu et rendre les cheveux gras. C'est une des raisons pour lesquelles se laver les cheveux tous les jours est très déconseillé avec un shampooing contenant des silicones. Il existe également de l'amodiméthicone, qui est un dérivé du diméthicone. Le polydiméthylsiloxane est un additif alimentaire (E900), utilisé comme antimoussant dans les boissons (Coca-Cola BlāK). La chaîne de poly(diméthylsiloxane) forme également la structure de base des huiles et des caoutchoucs silicones. Polymères -- Propriétés mécaniques Polymères -- Synthèse Polymères cationiques Polymères en émulsion Polymères ramifiés Polyuréthanes Résistance à l'humidité:Résistance à l'eau Revêtements en phase aqueuse Revêtements organiques Index. décimale : 667.9 Revêtements et enduits Résumé : Cationic waterborne polyurethanes (CWPUs) bring in hydrophilic component to molecular chain, which inevitably deteriorates its water-resistant ability. Here, we synthesized a series of branched chain cationic waterborne polyurethanes (i.e., CWPUs-Si) that had been modified using a novel star-branched polydimethylsiloxane (SB-PDMS) to improve their water-resistant performance. The effects of SB-PDMS content on the properties of the CWPUs-Si polymers (e.g., crystallinity, emulsion stability, mechanical performance, surface element enrichment, surface topography, water resistance), together with the performance of coatings prepared by cathodic electrodeposition, were determined. The results showed that the introduction of SB-PDMS increased phase separation and surface roughness induced by hydrogen bonding while the surface energy decreased, both of which improved water resistance. The polymers showed improved rigidity due to increased content of the hard segments and enhanced physical crosslinking. Except for an increase in pencil hardness, SB-PDMS had no effect on the films prepared by cathodic electrodeposition. The results from this study may provide a strategy to improve the water-resistant properties of CWPUs. Note de contenu : - EXPERIMENTAL : Materials - Synthesis of CWPUs-Si - Preparation of CWPUs-Si cast films and CED coatings - Characterization - RESULTS AND DISCUSSION : Synthesis and characterization of CWPUs-Si - Emulsion properties of the CWPUs-Si polymers - Surface element analysis of CWPUs-Si - Surface topography of CWPUs-Si - Water resistance of CWPUs-Si - Mechanical properties of CWPUs-Si - Properties of CED coatings prepared from the CWPUs-Si polymers - Table 1 : The composition design of CWPUs-Si - Table 2 : Table 2 Emulsion properties of CWPUs-Si polymers - Table 3 : Atomic mass contents of CWPUs-Si polymers DOI : https://doi.org/10.1007/s11998-021-00584-9 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00584-9.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38035 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23574	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)