Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane / Xiaolong Chen in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 19, N° 3 (05/2022)
![]()
[article]
Titre : Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane Type de document : texte imprimé Auteurs : Xiaolong Chen, Auteur ; Shusen Cao, Auteur ; Wangting Zhao, Auteur ; Lijun Chen, Auteur Année de publication : 2022 Article en page(s) : p. 887-895 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Acrylate d'hydroxyéthyle
Auto-réticulation
Caractérisation
Emulsifiants
Granulométrie
Latex
Polyacrylates
Réticulants en phase aqueuse
SilanesIndex. décimale : 667.9 Revêtements et enduits Résumé : The divinyl silane modified self-crosslinking polyacrylate latex was successfully prepared by semicontinuous seeded emulsion polymerization. Methyl methacrylate (MMA) and butyl acrylate (BA) were used as main monomers and the reaction was initiated by potassium persulfate (KPS). The modified monomer 1, 3-divinyltetramethyldisiloxane (DVMS) and crosslinked monomer hydroxyethyl acrylate (HEA) were introduced into the basic dispersion. Sodium dodecyl sulfonate (SDS) anionic surfactant and alkyl polyglycoside (APG) nonionic emulsifier were utilized as composite emulsifiers. The structure of latex film was characterized by Fourier transform infrared spectroscopy (FTIR). The latex films were tested by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and contact angle (CA) and apparent crosslinking percentage. The particle size of the emulsion was measured by Zetatrac dynamic light scattering instrument. The optimum conditions are as follows: the amount of composite emulsifier is 5.0%, the mass ratio of SDS to APG is 1:1, the amount of initiator is 0.5%, the amount of DVMS is 5.0%, and the amount of HEA is 1.0%. The emulsion has good mechanical stability and chemical stability, and the storage stability is ideal. The dispersion is blue and translucent, with a small particle size. The apparent crosslinking percentage of the latex film is above 89%, and the highest contact angle was more than 98°. The polyacrylate colloidal film prepared in this paper has outstanding thermal stability and hydrophobicity. Note de contenu : - EXPERIMENTAL : Materials - Preparation of self-crosslinking acrylic latex and its film - Characterizations
- RESULTS AND DISCUSSION : FTIR and DSC film analysis of the films - Influence of amount of initiator on conversion percentage and coagulation percentage - The effect of functional monomers on the apparent crosslinking percentage - Water absorption and contact angle of film - Thermal properties of the prepared latex films
- Table 1 : Recipe of self-crosslinking acrylic latex
- Table 2 : Influence of mass ratio of emulsifier on properties of latex
- Table 3 : Particle size of latexDOI : https://doi.org/10.1007/s11998-021-00566-x En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00566-x.pdf Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=38083
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 19, N° 3 (05/2022) . - p. 887-895[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 23605 - Périodique Bibliothèque principale Documentaires Disponible Preparation and properties of acrylic emulsion emulsified by reactive surfactants / Zheqing Gong in POLYMERS PAINT COLOUR JOURNAL - PPCJ, Vol. 212, N° 4674 (04/2022)
![]()
[article]
Titre : Preparation and properties of acrylic emulsion emulsified by reactive surfactants Type de document : texte imprimé Auteurs : Zheqing Gong, Auteur ; Wangting Zhao, Auteur ; Lijun Chen, Auteur Année de publication : 2022 Article en page(s) : p. 46-48 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Angle de contact
Caractérisation
Emulsifiants
Fumarate de dibutyle
Maléates
Polyacryliques
Polymères en émulsion
Surfactants réactifs
VinyltriéthoxysilaneIndex. décimale : 667.9 Revêtements et enduits Résumé : The acrylic emulsions were prepared successfully when the mixed monomers including dibutyl fumarate (DBF) and vinyl triethoxysilane (VTES) were initiated with KPS and emulsified with the mixed surfactants SR-10 and DOM. The prepared recipe was optimised and obtained as follows: the amount of emulsifiers was 5% ; the amount of initiator 0.4%, and amounts of the DBF and VETS were 5% and 2%, respectively. The prepared emulsion had good chemical and mechanical properties. The appearance of the resultant emulsion was translucent and light blue. The particle size of the resultant emulsion was in the range of 69nm to 105nm and the distribution was very narrow. Note de contenu : - EXPERIMENTAL : Materials - Preparation of acrylic emulsion - Characterisations
- RESULTS AND DISCUSSION : FTIR of film - DSC of film - Determination of amount of emulsifiers - Determination of amount of initiator - Contact angle of film
- Table 1 : Influence of amount of emulsifiers on emulsion propertiesEn ligne : https://drive.google.com/file/d/1pMtJyhAf8Oh1Dctr9Ze1Od_46MNY5Btx/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37392
in POLYMERS PAINT COLOUR JOURNAL - PPCJ > Vol. 212, N° 4674 (04/2022) . - p. 46-48[article]Réservation
Réserver ce document
Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité 23336 - Périodique Bibliothèque principale Documentaires Disponible Study on influencing factors of stability of acrylate cathodic electrodeposition coatings / Xu Conghui in POLYMERS PAINT COLOUR JOURNAL - PPCJ, Vol. 212, N° 4675 (06/2022)
![]()
[article]
Titre : Study on influencing factors of stability of acrylate cathodic electrodeposition coatings Type de document : texte imprimé Auteurs : Xu Conghui, Auteur ; Zheqing Gong, Auteur ; Wangting Zhao, Auteur ; Lijun Chen, Auteur Année de publication : 2022 Article en page(s) : p. 49-51 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation
Dépôt électrolytique
Polyacrylates
Réticulants
Revêtements -- Stabilité
Revêtements organiquesIndex. décimale : 667.9 Revêtements et enduits Résumé : The stability of the CED coatings is vital to their storage and application, which have an important effect on the film of the CED coatings. In this work, CED coatings were prepared by mixing the synthetic resin and blocked isocyanate. The factors, which have an influence on the stability of the CED coatings, were studied and optimised. The optimum conditions for preparing the CED coatings with good stability are the following. The mixing process is that the resin and curing agent is mixed well, and then water is added to disperse in the blender. The rotational speed and dispersed time were 900r/min and 40min, respectively. TDI trimer was the curing agent of the CED coating. The neutralisation degree was 80%. Note de contenu : - EXPERIMENTAL : Materials - Preparation of CED coatings - Characterisation
- RESULTS AND DISCUSSION : Influence of mixed process on stability of CED coatings - Effect of agitation on the stability of CED coatings - Determination of curing agent - Influence of components of cationic acrylate resin on stability of CED coatings
- Table 1 : Effect of mixing process on stability of CED coatings
- Table 2 : Influence of agitation on stability of CED coatings
- Table 3 : Main parameters of curing agents
- Table 4 : Effec(ts of curing agent on stability of CED coatings
- Table 5 : Influences of different amine value and hydroxyl value on appearance and stability of CED coatingsEn ligne : https://drive.google.com/file/d/19TTEkh3IzJZZBS5kdemEFqnTBsaj3pND/view?usp=drive [...] Format de la ressource électronique : Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=37786
in POLYMERS PAINT COLOUR JOURNAL - PPCJ > Vol. 212, N° 4675 (06/2022) . - p. 49-51[article]Réservation