Titre : |
Healing performance of a self-healing protective coating according to damage width |
Type de document : |
texte imprimé |
Auteurs : |
Dong-Min Kim, Auteur ; Lee Junseo, Auteur ; Ju-Young Choi, Auteur ; Seung-Won Jin, Auteur ; Kyeong-Nam Nam, Auteur ; Hyeong-Ju Park, Auteur ; Seung-Hyun Lee, Auteur ; Chan-Moon Chung, Auteur |
Année de publication : |
2022 |
Article en page(s) : |
p. 45-49 |
Note générale : |
Bibliogr. |
Langues : |
Anglais (eng) |
Catégories : |
Analyse de dommages (matériaux) Encapsulation Essais (technologie) Essais accélérés (technologie) Huile de linL'huile de lin ou "huile de graines de lin" est une huile de couleur jaune d'or, tirée des graines mûres du lin cultivé, pressées à froid et/ou à chaud ; parfois elle est extraite par un solvant, en vue de l'usage industriel ou artistique, principalement comme siccatif, ou huile auto-siccative.
Les utilisations de l'huile de lin dérivent de sa richesse en acides gras polyinsaturés, en particulier en acides linolénique et linoléique, qui lui doivent leur nom.
L'huile de lin polymérise spontanément à l'air, avec une réaction exothermique : un chiffon imbibé d'huile peut ainsi, dans certaines conditions, s'enflammer spontanément.
Pour ses propriétés de polymère, l'huile de lin est employée seule, ou mélangée à d'autres huiles, résines et solvants, et est utilisée en tant que : Imprégnateur et protecteur des bois à l'intérieur comme à l'extérieur : protection contre l'humidité, les champignons et insectes, et contre la poussière par son caractère antistatique, composant de certains vernis de finition, liant de broyage pour la peinture à l'huile, agent plastifiant du mastic de vitrier, agent durcisseur de diverses préparations, agent de cohérence et liant dans la fabrication du linoléum. Humidité -- Absorption:Eau -- Absorption Ions chlorure Matériaux cimentaires -- Revêtements protecteurs Microcapsules Pénétration (physique) Polyéthylène greffé anhydride maléique Revêtement autoréparant
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
Although self-healing protective coatings have been widely studied, systematic research on healing performance of the coating according to damage width has been rare. In addition, there has been rare reports of self-healing of the protective coating having damage width wider than 100pm. In this study, self-healing performance of a microcapsule type self-healing protective coating on cernent mortar was studied for the coating with damage width of 100-300pm. The effect of capsule-loading (20wt%, 30wt% and 40wt%), capsule size (65,102 and 135pm mean diameter) and coating thickness (50, 80 and 100pm thick undercoating) on healing efficiency was investigated by water sorptivity test. Accelerated carbonation test, chloride ion penetration test and scanning electron microscope (SEM) study were conducted for the self-healing coating with a 300pm wide damage. Healing efficiency of the self-healing coating decreased with increasing damage width. As capsule-loading, capsule size or coating thickness increased, healing efficiency of the self-healing coating increased. Healing efficiency of 76% or higher was achieved using the self-healing coating with a 300pm wide scratch. The self-healing coating with a 200pm wide crack showed healing efficiency of 70% or higher. The self-healing coating having a 300pm-wide scratch showed effective protection of the substrate mortar from carbonation and chloride ion penetration, which was supported by SEM study. |
Note de contenu : |
- MATERIALS AND METHODS : Materials - Instruments - Microencapsulation of linseed oil - Preparation of coating samples - Vater sorptivity test - Determination of healing efficiency - Accelerated carbonation test - Chloride ion penetration test
- RESULTS AND DISCUSSION : Microcapsules - Water sorptivity test - Other performances of the self-healing coating with damage width of 300µm
- Table 1 : Variable parameters of the coating samples |
En ligne : |
https://drive.google.com/file/d/1NwpVSD-cYsSHt18KguwcleHTKg7yDeHh/view?usp=drive [...] |
Format de la ressource électronique : |
Pdf |
Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36974 |
in POLYMERS PAINT COLOUR JOURNAL - PPCJ > Vol. 212, N° 4673 (02/2022) . - p. 45-49
[article]
|