Synergistic flame-retardant effect of aluminum diethyl phosphinate in PP/IFR system and the flame-retardant mechanism / J.-L. Li in INTERNATIONAL POLYMER PROCESSING, Vol. 36, N° 5 (2021)  

[article]  inINTERNATIONAL POLYMER PROCESSING > Vol. 36, N° 5 (2021) . - p. 519-528 Titre : Synergistic flame-retardant effect of aluminum diethyl phosphinate in PP/IFR system and the flame-retardant mechanism Type de document : texte imprimé Auteurs : J.-L. Li, Auteur ; C.-T. Gao, Auteur ; X. Sun, Auteur ; S.-G. Peng, Auteur ; Y.-W. Wang, Auteur ; S.-H. Qin, Auteur Année de publication : 2021 Article en page(s) : p. 519-528 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Caractérisation Carbonisation Chimie analytique Combustion Diéthylphosphinate d'aluminium Formulation (Génie chimique) Intumescence (chimie) Polymères ignifuges Polypropylène Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Index. décimale : 668.4 Plastiques, vinyles Résumé : Synergistic flame-retardant effect of aluminum diethyl phosphinate (AlPi) in intumescent flame retardant polypropylene (PP/IFR) system and the flame-retardant mechanism were investigated. The flame retardancy of PP/IFR/AlPi (the mass ratio of IFR to AlPi is 2 : 1) was the best, which was proved by the results of the limiting oxygen index (LOI) test, UL-94 test, and cone calorimeter test ( CCT) test. Here, the LOI value of the sample was as high as 34% and passed the V–0 rating in UL–94 test. The peak heat release rate (PHRR) decreased by 92.57%, the total heat release (THR) reduced by 90.52%. Thermogravimetric (TGA) data showed that the introduction of AlPi improved thermal stability and changed the thermal degradation behavior of PP/IFR composites. Interestingly, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDXS) and laser Raman spectroscopy (LRS) proved that PP/IFR/AlPi had formed more residual carbon, but the flame retardancy was worse than PP/IFR/AlPi. This is because when the mass ratio of IFR to AlPi is 2 : 1, the synergy between IFR and AlPi was significant, gas-phase flame retardant and condensed-phase flame retardant reached a balance and obtained the best flame retardant effect. Note de contenu : - EXPERIMENTAL : Materials - Preparation of PP/IFR/AlPi composites - Characterization - RESULTS AND DISCUSSION : Flame retardancy of PP/IFR/AlPi composites - Combustion behavior of PP/IFR/AlPi composites - Thermal degradation behavior of PP/IFR/AlPi composites - Residual carbon morphology of PP/IFR/AlPi composites - Chemical composition of residual carbon in PP/IFR/AlPi composites - POSSIBLE FLAME-RETARDANT MECHANISM DISCUSSION - Table 1 : Formulations of PP/IFR/AlPi composites - Table 2 : Results of the LOI and UL-94 tests for PP, PP/IFR/AlPi, PP/IFR, PP/AlPi composites - Table 3 : CCT results of PP, PP/IFR/AlPi, PP/IFR, PP/AlPi composites - Table 4 : TGA and DTG data for PP, PP/IFR/AlPi, PP/IFR, PP/AlPi composites - Table 5 : Chemical composition of the residue chars for PP, PP/IFR/AlPi, PP/IFR and PP/AlPi composites DOI : https://doi.org/10.1515/ipp-2020-4082 En ligne : https://drive.google.com/file/d/1OfUxCdiYtuNX7vTx3Q9KvyYy0W2T1KXk/view?usp=shari [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36519 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
23735	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)