Evaluation of linear and nonlinear rheology of microfibrillated cellulose / Sweta Sarangi in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 5 (09/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 5 (09/2021) . - p. 1401-1411 Titre : Evaluation of linear and nonlinear rheology of microfibrillated cellulose Type de document : texte imprimé Auteurs : Sweta Sarangi, Auteur ; Suresh Kumar Yatirajula, Auteur ; Vinod Kumar Saxena, Auteur Année de publication : 2021 Article en page(s) : p. 1401-1411 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Caractérisation Cisaillement (mécanique) Fibres cellulosiques Loi de puissance La loi de puissance est une relation mathématique entre deux quantités. Si une quantité est la fréquence d'un évènement et l'autre est la taille d'un évènement, alors la relation est une distribution de la loi de puissance si les fréquences diminuent très lentement lorsque la taille de l'évènement augmente. En science, une loi de puissance est une relation entre deux quantités x et y qui peut s'écrire de la façon suivante : y = a x k {\displaystyle y=ax^{k}} y=ax^{k} où a est une constante dite constante de proportionnalité et k est une autre constante, dite exposant, puissance, indice ou encore degré de la loi. On observe des lois de puissance dans beaucoup de domaines scientifiques (physique, biologie, psychologie, sociologie, économie, linguistique). Elles permettent en effet de décrire tous les phénomènes qui présentent une invariance d'échelle. Rhéologie Tension superficielle Viscoélasticité Index. décimale : 667.9 Revêtements et enduits Résumé : Microfibrillated cellulose (MFC) is a noble class of material that has drawn considerable attention due to its numerous properties such as mechanical robustness, high aspect ratio, lower coefficient of thermal expansion, water retention ability, barrier properties to oxygen, compatibility with biomaterials, biodegradability, large surface area and interesting rheology. This present work deals with the rheology of MFC suspension in water. The effect of temperature on the concentration of the suspension of MFC was studied. Three regimes of MFC were observed for the shear rate lying in the range of 0.01–1000 s−1, supported by a buildup of a network of hydroxyl groups present on the surface, resulting in shear thinning, shear thickening, and shear thinning regions, respectively. An increase in the concentration of MFC, increased viscosity, and the dominance of storage modulus were observed. A high value of storage modulus indicates a higher degree of crosslinking of fibrils. The experimental data were well fitted by using the Ostwald-de Waele power law model. The results suggested that an increase in the temperature did not have any significant effect on the MFC rheology in the temperature range of 25–60°C. The Gaussian process regression model was used to determine the performance parameters. Dynamic oscillatory measurements were performed to validate the viscoelastic behavior. Note de contenu : - EXPERIMENTAL : Materials - FTIR analysis - Morphology - Interfacial tension measurement - Rheological measurement - Power-law model - Gaussian process regression model RESULTS AND DISCUSSION : Structural and physical characterization - Interfacial tension measurement - Rheological studies - Table 1 : Main spectral peaks with band assignments of the functional groups for MFC - Table 2 : Effect of temperature on three different regions in terms of shear rate (s−1) range and Ostwald-de Waele power law model parameters for 2% aqueous MFC suspensions - Table 3 : The GPR fitting parameters for the aqueous suspension of MFC at different temperatures DOI : https://doi.org/10.1007/s11998-021-00505-w En ligne : https://link.springer.com/content/pdf/10.1007/s11998-021-00505-w.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36442 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22991	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)