Polyurethane electrospun fiber biomimetics membrane for constructing the structure of grain layer with good breathability for cattle split leather / Nan Chen in JOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA), Vol. CXVI, N° 8 (08/2021)  

[article]  inJOURNAL OF THE AMERICAN LEATHER CHEMISTS ASSOCIATION (JALCA) > Vol. CXVI, N° 8 (08/2021) . - p. 284-289 Titre : Polyurethane electrospun fiber biomimetics membrane for constructing the structure of grain layer with good breathability for cattle split leather Type de document : texte imprimé Auteurs : Nan Chen, Auteur ; Yanchun Li, Auteur ; Jianbo Qu, Auteur ; Jian-Yong Wang, Auteur Année de publication : 2021 Article en page(s) : p. 284-289 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Air Caractérisation Chimie biomimétique Cuir Electrofilature Essais accélérés (technologie) Membranes imper-respirantes Mousses plastiques Perméabilité Polyuréthanes Tissés Vapeur d'eau Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : The traditional thick coating on split leather does not have the ability to breathe like full grain leather. The air and water vapor permeabilities of full grain leather are well known properties due to its fiber woven structure. Simulating the fiber morphology and weaving structure of the dermis or grain layer is very important to construct a top surface layer for split leather. In this paper, a PU (polyurethane) foam layer is put first on the split to enhance the adhesion of a second application of a superfine fibrous PU resin. This foam uses well-known waterborne polyurethane foaming technology. This dried foam has good breathability because of high porosity. A superfine fiber membrane is next put atop of the foam layer by using an electro-spun polyurethane resin. This second resin imitates collagen fibers in the network structure of the leathers’ grain layer. Thus, this resultant electrospun fiber biomimetics membrane simulated the grain layer of natural leather. SEM showed the morphology and structure of this electrospun fiber biomimetic membrane to be like that of the grain layer of natural leather. The porosity and apparent density were basically the same as the grain of leather, which were 63.65% and 583.878 kg/m3 respectively. The air and water vapor permeability of the biomimetics membrane were also as high as 2250 mL·cm-2·h-1 and 8753.02 μg·cm-2·h-1 respectively. Therefore, the biomimetics membrane largely restored the ability to breathe of split leather. Thus, this method simulates the performance and structure of full grain leather and is a novel method for industrial production. Note de contenu : - EXPERIMENTAL : Materials and instruments - Preparation of the biomimetics electrospun fiber coating - CHARACTERIZATION : Morphology observation - Porosity and apparent density analyses - Air permeability and water vapor permeability analyses - RESULTS AND DISCUSSION : SEM observation of the surface and longitudinal of the sample - Test for air permeability and water vapor permeability DOI : https://doi.org/10.34314/jalca.v116i8.4358 En ligne : https://drive.google.com/file/d/1YepXdwsWoigjZKA57PKF4GCbf594UtuZ/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=36085 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22875	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)