Investigation of the wettability, anticorrosion, and accelerated weathering behaviors of siloxane-modified acrylic resin and functionalized graphene nanocomposite coatings on LY12 aluminum alloy / Paul C. Uzoma in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 3 (05/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 3 (05/2021) . - p. 789-806 Titre : Investigation of the wettability, anticorrosion, and accelerated weathering behaviors of siloxane-modified acrylic resin and functionalized graphene nanocomposite coatings on LY12 aluminum alloy Type de document : texte imprimé Auteurs : Paul C. Uzoma, Auteur ; Qiumeng Wang, Auteur ; Wanyu Zhang, Auteur ; Ning Jie Gao, Auteur ; Fuchun Liu, Auteur ; En-Hou Han, Auteur Année de publication : 2021 Article en page(s) : p. 789-806 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Aluminium -- Alliages Anticorrosifs Anticorrosion Caractérisation Graphène Le graphène est un cristal bidimensionnel (monoplan) de carbone dont l'empilement constitue le graphite. Il a été isolé en 2004 par Andre Geim, du département de physique de l'université de Manchester, qui a reçu pour cette découverte le prix Nobel de physique en 2010 avec Konstantin Novoselov. Il peut être produit de deux manières : par extraction mécanique du graphite (graphène exfolié) dont la technique a été mise au point en 2004, ou par chauffage d'un cristal de carbure de silicium, qui permet la libération des atomes de silicium (graphène epitaxié). Record en conduction thermique jusqu'à 5300 W.m-1.K-1. C'est aussi un matériaux conducteur. Hydrophobie Matériaux hybrides Métaux -- Revêtements protecteurs Mouillabilité Polyacryliques Revêtements organiques Siloxanes Les siloxanes sont une classe de composés du silicium dont la formule empirique est R2SiO, où R est un groupe radical qui peut être organique. Des exemples représentatifs sont [SiO(CH3)2]n (diméthylsiloxane) et [SiO(C6H5)2]n (diphénylsiloxane), où n est typiquement supérieur à 4. Ces composés peuvent être des hybrides organiques et inorganiques. Les chaînes organiques confèrent au composé des propriétés hydrophobes alors que la chaîne principale -Si-O-Si-O- est purement inorganique. Le mot siloxane est dérivé de Silicium, Oxygène et alkane. Des siloxanes peuvent être trouvés dans des produits tels que des cosmétiques, des déodorants, des enduits hydrophobes pour pare-brise, des peintures et certains savons. Les siloxanes polymérisés (polysiloxanes) sont appelés silicones1,2. Le siloxane est massivement utilisé dans l'industrie cosmétique (rouges à lèvre, conditionneurs et shampooings, déodorants, etc.). Une application récente du Siloxane D5 (2001) a été trouvée dans le nettoyage à sec des textiles en remplacement du perchloroéthylène. Ce procédé est très répandu aux États-Unis et au Royaume-Uni. Il devient de plus en plus courant en Europe continentale dont la France, afin de promouvoir l'usage de procédés écologiques et respectueux de la santé humaine. Index. décimale : 667.9 Revêtements et enduits Résumé : To expand the applications of graphene which has so far been limited by the expensive nature of single-layer graphene, the effects of varying percentages of low-cost functionalized multilayer graphene nanosheets in siloxane-modified organic coatings were studied. The hydrophobic organic siloxane–acrylic resin was prepared by solution polymerization of acrylic monomers, and the graphene nanosheets were functionalized using fluorosilane. The coatings were sprayed on the LY12 aluminum substrate, and the wettability, anticorrosion, conductive, and accelerated weathering behaviors were comprehensively examined. It is shown that the increasing addition of functionalized graphene nanosheets increases the water contact angle and the surface conductivity. At 5% graphene loading, coating–substrate adhesion remains almost unchanged, while the electrochemical impedance parameters revealed good anticorrosion performance up to 10% loading. The surface measurements and Fourier transform infrared spectroscopy (FTIR) results confirmed the photostabilization ability of graphene loading in acrylic coatings during the accelerated weathering test. Also, the mechanical properties of the coatings were not damaged during the exposure, and pitting corrosion sites were observed only on the 20% graphene-filled coatings after 1000 h of exposure. These integrated analyses of mechanical properties and environmental accelerated tests are beneficial to engineering applications of graphene coatings. Note de contenu : - EXPERIMENTAL : Materials - Coatings preparation - Apparatus and measurement - RESULTS AND DISCUSSION : XPS survey of the functionalized graphene nanosheets - Raman spectroscopy, TEM, and wettability analysis of the functionalized graphene nanosheets - Surface wettability analysis - EIS measurements - Surface resistivity test - Wet adhesion strength - Accelerated weathering test DOI : https://doi.org/10.1007/s11998-020-00443-z En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00443-z.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=35930 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22785	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)