Morphology-dependent optical and wetting behavior of GLAD PTFE thin films / Rajnarayan De in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 18, N° 1 (01/2021)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 18, N° 1 (01/2021) . - p. 173-182 Titre : Morphology-dependent optical and wetting behavior of GLAD PTFE thin films Type de document : texte imprimé Auteurs : Rajnarayan De, Auteur ; S. Maidul Haque, Auteur ; Ranveer Singh, Auteur ; C. B. Basak, Auteur ; S. Jena, Auteur ; J. S. Misal, Auteur ; D. D. Shinde, Auteur ; Tapobrata Som, Auteur ; K. Divakar Rao, Auteur Année de publication : 2021 Article en page(s) : p. 173-182 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anti-réflectance Caractérisation Dépôt à angle de regard Hydrophobie Polytétrafluoréthylène Revêtement auto-nettoyant Revêtements organiques Transmittance La transmittance, en général, est le rapport caractérisant la transmission d'une grandeur dans un système. Elle se calcule par le rapport entre la grandeur en entrée et en sortie. En optique, la transmittance d'un matériau ou d'un filtre est la fraction du flux lumineux le traversant. Elle est également nommée facteur de transmission mais aussi transparence dans le domaine de la photographie. Index. décimale : 667.9 Revêtements et enduits Résumé : E-beam evaporation equipped with glancing angle deposition arrangement (GLAD) was used to fabricate nanostructured polytetrafluoroethylene (PTFE) films in a single-step coating process. Three sets of PTFE coatings were prepared using various oblique angles, e-beam currents, and deposition times to explore the effects of deposition parameters on the properties of PTFE nanostructured coatings. Water contact angle (WCA) of the coatings was found to be enhanced with the increase in all the above process parameters. Optical transmittance of the coatings was also found to be improved with the above parameters except for in the case of an increase in thickness of the films (in very high thickness region), where the transmittance was degraded due to light scattering from the sample surface. After all the optimizations, the ~ 130-nm-thick GLAD PTFE sample prepared with highest e-beam current was found to be more suitable for antireflection and self-cleaning applications. The single-sided coating demonstrates a very high average transmittance of ~ 95.6% (with a wideband transmittance spectrum among the others) in the visible and NIR wavelength range with excellent self-cleaning nature (WCA ~ 156°, sliding angle ~ 10°). The trend of measured WCA with respect to surface roughness follows the Cassie–Baxter model. Overall, the study demonstrates the possibility of fabricating highly transparent self-cleaning coatings using the GLAD technique, which is potentially useful for fabricating protecting cover glasses in solar panels. Note de contenu : - EXPERIMENTAL DETAILS : Fabrication of the nanostructured PTFE films - Characterization of the films - RESULTS AND DISCUSSION : Effect of deposition angle on the film properties - Effect of e-beam current on the films - Effect of film thickness on CA and transmittance of the coatings - THEORETICAL CALCULATION OF WCA ON THE ROUGH SURFACES - Table 1 and 2 : RMS roughness data of the films prepared at different oblique angles DOI : https://doi.org/10.1007/s11998-020-00395-4 En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00394-5.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=35361 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22605	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)