Evaluation of cut-edge corrosion in environmentally friendly waterborne coil-coatings using the Scanning Vibrating Electrode Technique (SVET) / S. Sheikholeslami in SURFACE COATINGS INTERNATIONAL, Vol. 103.5 (09-10/2020)  

[article]  inSURFACE COATINGS INTERNATIONAL > Vol. 103.5 (09-10/2020) . - p. 258-261 Titre : Evaluation of cut-edge corrosion in environmentally friendly waterborne coil-coatings using the Scanning Vibrating Electrode Technique (SVET) Type de document : texte imprimé Auteurs : S. Sheikholeslami, Auteur ; L. Gommans, Auteur ; S. Morrison, Auteur ; G. Williams, Auteur ; H. N. McMurray, Auteur ; P. Morgan, Auteur ; C. Lowe, Auteur ; D. Williams, Auteur ; W. Gao, Auteur Année de publication : 2020 Article en page(s) : p. 258-261 Note générale : Bibliogr. Langues : Anglais (eng) Catégories : Acier L'acier est un alliage métallique utilisé dans les domaines de la construction métallique et de la construction mécanique. L'acier est constitué d'au moins deux éléments, le fer, très majoritaire, et le carbone, dans des proportions comprises entre 0,02 % et 2 % en masse1. C'est essentiellement la teneur en carbone qui confère à l'alliage les propriétés du métal qu'on appelle "acier". Il existe d’autres métaux à base de fer qui ne sont pas des aciers comme les fontes et les ferronickels par exemple. Anticorrosifs Anticorrosion Coil coatings Métaux -- Revêtements protecteurs Revêtements en phase aqueuse:Peinture en phase aqueuse Index. décimale : 667.9 Revêtements et enduits Résumé : There is an increasing demand for painted galvanised steels for building applications worldwide, and great efforts are being made to improve the corrosion behaviour of coil coatings in order to reduce relevants costs. Evaluating corrosion resistance in painted coils was mainly done via the natural exposure test, following a standardised process at exposure sites, until accelerated corrosion tests such as salt spray and cyclic corrosion test were finally introduced. Theses tests reinforce the need for a laboratory method of predicting long term performance of corrosion-protective coatings in an accelerated timescale. Cut edge in painted coils is one of the main sites where coating failure initiates. Since the steel substrate in coil coating is fully exposed at the cut-edge, the galvanic coupling causes noticeable corrosion and paint delamination (a phenomenon reffered to as "undercutting") over time. Therefore, several studies in this area were performed to understand and, more importantly, tried to correlate lab results to long term weathering exposure performance. In this study, we have utilised an electrochemical scanning technique to analyse corrosion at the cut-edge of fully commercialised environmental-friendly coating systems and benchmarked these results natural exposure assessments for the first time. Note de contenu : - Introduction to Scanning Vibrating Electrode Technique (SVET) - Rapid corrosion assessment by SVET - Fig. 1 : Schematic and in-operation views of the SVET probe for corrosion studies - Fig. 2 : SVET current density maps of A) P1, B) P2 and C) P3 after 12 hours in 5 wt. % NaCl solution - Fig. 3 : SVET current density maps of A) P1, B) P2 and C) P3 after 24 hours in 5 wt. % NaCl solution - Fig. 4 : Total mass loss comparison of P1, P2 and P3 after 24 hours in 5 wt. % NaCl solution using SVET - Fig. 5 : Naturally-exposed panels at Muriwai beach ; A) P1, B) P2 and C) P3 coating systems after ten months of unwashed exposure Table 1 : Edge creep analysis of panels according to the AS/NZS 2728 standard En ligne : https://drive.google.com/file/d/1pTuj5Sq_79AYW55ZUNS7Hv7GzdkGscI7/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34727 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22306	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)