Hydrophilic nano-SiO2/PVA-based coating with durable antifogging properties / Guoqiang Wu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 17, N° 5 (09/2020)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 17, N° 5 (09/2020) . - p. 1145–1155 Titre : Hydrophilic nano-SiO2/PVA-based coating with durable antifogging properties Type de document : texte imprimé Auteurs : Guoqiang Wu, Auteur ; Yuling Yang, Auteur ; Yongtong Lei, Auteur ; Dapeng Fu, Auteur ; Yuchao Li, Auteur ; Yanhu Zhan, Auteur ; Jinming Zhen, Auteur ; Mouyong Teng, Auteur Année de publication : 2020 Article en page(s) : p. 1145–1155 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Angle de contact Caractérisation Chimie des surfaces Dioxyde de silicium Essais (technologie) Hydrophilie Mélanges (chimie) Morphologie (matériaux) Mouillabilité Polyacétate de vinyle Revêtements -- Propriétés mécaniques Revêtements -- Propriétés optiques Revêtements anti-buée Transmittance La transmittance, en général, est le rapport caractérisant la transmission d'une grandeur dans un système. Elle se calcule par le rapport entre la grandeur en entrée et en sortie. En optique, la transmittance d'un matériau ou d'un filtre est la fraction du flux lumineux le traversant. Elle est également nommée facteur de transmission mais aussi transparence dans le domaine de la photographie. Index. décimale : 667.9 Revêtements et enduits Résumé : Hydrophilic SiO2/poly(vinyl alcohol) (PVA) coating prepared by solution blended method showed high light transmittance and durable antifogging performance. The effects of SiO2 content and pH value of SiO2 suspension on the morphology and properties of hydrophilic coating were studied by Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy, contact angle test, ultraviolet visible light spectrophotometer, and antifogging test. Results showed that the PVA had good compatibility with nano-SiO2 because of the formation of Si–O–C chemical bond at the interface between nano-SiO2 and PVA. When prepared at pH = 7, SiO2/PVA coatings (SiO2/PVA mass ratio of 0.8) were hydrophilic, with a water contact angle of 22.9°, and exhibited papilla-like surface features (RMS = 7.6 nm). Polyethylene (PE) samples coated with this SiO2/PVA film exhibited a light transmittance of up to 90%, between 560 and 700 nm, and remained fog-free for more than 1 month after exposure to water at 60°C (QB/T 4475-2013 standard). Water-resisting and wear-resisting tests revealed that antifogging coatings demonstrated excellent mechanical properties. Note de contenu : - EXPERIMENTAL : Material - Preparation - Characterization - RESULTS AND DISCUSSION : Chemical composition - Surface morphology - Surface wettability - The fogging test and optical properties - The mechanical properties DOI : https://doi.org/10.1007/s11998-020-00338-z En ligne : https://link.springer.com/content/pdf/10.1007/s11998-020-00338-z.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34563 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
22303	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)