Preparation and performance of waterborne polyurethane modified by cross-linking of aziridine/carboxylated multi-walled carbon nanotubes / Ma Xingyuan in JOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC), Vol. 104, N° 4 (07-08/2020)  

[article]  inJOURNAL OF THE SOCIETY OF LEATHER TECHNOLOGISTS & CHEMISTS (JSLTC) > Vol. 104, N° 4 (07-08/2020) . - p. 196-200 Titre : Preparation and performance of waterborne polyurethane modified by cross-linking of aziridine/carboxylated multi-walled carbon nanotubes Type de document : texte imprimé Auteurs : Ma Xingyuan, Auteur ; Wu Xiaozhen, Auteur ; Ding Bo, Auteur ; He Yuanxin, Auteur ; He Yinghua, Auteur ; Zheng Silong, Auteur Année de publication : 2020 Article en page(s) : p. 196-200 Note générale : Bibliogr.ZAZ Langues : Anglais (eng) Catégories : Allongement à la rupture Aziridine L'aziridine (n.f.) ou azacyclopropane est le composé organique cyclique de formule brute C2H5N. Elle est aussi le composé parent des aziridines et du groupe fonctionnel qui correspond à un hétérocycle à trois côtés composé d'une amine et de deux groupes méthylène. Caractérisation Carboxylation Couches minces -- Propriétés mécaniques Cuir Essais (technologie) Greffage (chimie) Humidité -- Absorption:Eau -- Absorption Nanotubes de carbone à parois multiples Un nanotube de carbone multifeuillet est constitué de plusieurs feuillets de graphènes enroulés les uns autour des autres. Il existe deux modèles pour décrire la structure des nanotubes multifeuillets : - le modèle poupée russe: les plans de graphène sont arrangés en cylindres concentriques ; - le modèle parchemin: un seul feuillet de graphène est enroulé sur lui-même, comme une feuille de papier. Polymères en émulsion Polyuréthanes Résistance à l'humidité:Résistance à l'eau Résistance à la traction Réticulation (polymérisation) Index. décimale : 675 Technologie du cuir et de la fourrure Résumé : Carboxylated multi-walled carbon nanotubes (MWCNT-COOH) were prepared by treating multiwalled carbon nanotubes (MWCNT) with concentrated sulfuric acid (H,SO4) and concentrated nitric acid (HNO3) at a volume ratio of 3:1. Afterwards, taking MWCNT-COOH as the modified materials and aziridine (AZ) as the cross-linking agents were added to polyether-based waterborne polyurethane (WPU) thus preparing waterborne polyurethane modified by cross-linking of aziridine/carboxylated multi-walled carbon nanotubes (AZ-MWCNT-COOH-WPU) emulsion and films. The latter was applied to the surface treatment of natural leather and synthetic leather and other coating materials. The effects of different AZ contents on the water resistance and mechanical properties of AZ-MWCNT-COOH-WPU films were analysed and are discussed. The synthesised product was characterised by FTIR, XRD, SEM and other detection methods. The results showed that AZ successfully grafted MWCNT-COOH to the molecular chain of WPU and, when the content of AZ increased, the tensile strength of AZ-MWCNT-COOH-WPU film increased, firstly from 14.8MPa to 21.8MPa and then decreased to 12.1MPa. Elongation at break decreased from 570.2% to 198.4%, the water absorption decreased from 108.9% to 2.4% thus the water resistance was enhanced. Note de contenu : - EXPERIMENTAL PROCEDURE : Experiment materials and instrubments - Preparation of MWCNT-COOH - Preparation of AZ-MWCNT-COOH-WPU emulsion - Preparation of AZ-MWCNT-COOH-WPU film - Characterisation and test methods - RESULTS AND DISCUSSIONS : FTIR analysis of MWCNT-COOH - Mechanical properties of AZ-MWCNT-COOH-WPU films - Water resistance analysis of AZ-MWCNT-COOH-WPU films - SEM analysis of AZ-MWCNT-COOH-WPU films En ligne : https://drive.google.com/file/d/1-LHZ2ykQRApgvR0NWf-_GkwPDD_IfZWI/view?usp=drive [...] Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=34333 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21881	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)