Synthesis and properties of SrSn(OH)6 nanorods and their flame retardancy and smoke suppression effects on epoxy resin / Danqi Yang in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 16, N° 6 (11/2019)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 16, N° 6 (11/2019) . - p. 1715-1725 Titre : Synthesis and properties of SrSn(OH)6 nanorods and their flame retardancy and smoke suppression effects on epoxy resin Type de document : texte imprimé Auteurs : Danqi Yang, Auteur ; Chong Zhang, Auteur ; Luming Dong, Auteur ; Xudong Huo, Auteur ; Weikang Zheng, Auteur ; Jianzhong Xu, Auteur ; Haiyun Ma, Auteur Année de publication : 2019 Article en page(s) : p. 1715-1725 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anti-fumée Combustion Epoxydes Hydroxystannate de strontium Ignifugeants Composé chimique utilisé pour réduire l'inflammabilité. Il peut être incorporé au produit durant sa fabrication ou appliqué ultérieurement à sa surface. Matériaux hybrides -- Propriétés thermiques Nanoparticules Pyrolyse La pyrolyse est la décomposition ou thermolyse d'un composé organique par la chaleur pour obtenir d'autres produits (gaz et matière) qu'il ne contenait pas. L'opération est réalisée en l'absence d'oxygène ou en atmosphère pauvre en oxygène pour éviter l'oxydation et la combustion (L’opération ne produit donc pas de flamme). Il s'agit du premier stade de transformation thermique après la déshydratation. Elle permet généralement d'obtenir un solide carboné, une huile et un gaz. Elle débute à un niveau de température relativement bas (à partir de 200 °C) et se poursuit jusqu'à 1 000 °C environ. Selon la température, la proportion des trois composés résultants est différente. Revêtements protecteurs Index. décimale : 667.9 Revêtements et enduits Résumé : A nanorod-structured strontium hydroxystannate [SrSn(OH)6] flame retardant was synthesized via a facile coprecipitation method and employed in epoxy resin (EP). Based on X-ray diffraction analysis, scanning electron microscopy, and transmission electron microscopy, the as-synthesized SrSn(OH)6 nanorods exhibited high crystallinity and uniform size distribution. The flame retardancy and smoke suppression properties of EP/SrSn(OH)6 composites were investigated by limiting oxygen index and cone calorimetry tests. The results showed that incorporation of SrSn(OH)6 led to a dramatic reduction of the fire hazards of EP, including a 21.9% maximum decrease in the peak heat release rate, a 33.3% reduction in the toxic CO yield, and a 133.3% increase in the char residue. In particular, this is the first attempt to evaluate the flame retardancy properties of SrSn(OH)6 nanorods in EP. The improved flame retardancy properties of the SrSn(OH)6 nanorods is attributed to their catalytic carbonization effect. Note de contenu : - EXPERIMENTAL : Materials and methods - Preparation of SrSn(OH)6 nanorods - Preparation of EP/SrSn(OH)6 composites - Characterization and analysis - RESULT AND DISCUSSION : Structure and morphology of SrSn(OH)6 nanorods - Thermal degradation of SrSN(OH)6 nanorods - Thermal properties of EP/SrSN(OH)6 nanocomposites - Combustion behavior of EP/SrSN(OH)6 nanocomposites - Flame-retardant mechanism of SrSN(OH)6 - Compliance with ethical standards - Conflict of interest DOI : 10.1007/s11998-019-00254-x En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-019-00254-x.pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33425 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21321	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)