UV-curable waterborne polyurethane dispersions modified with a trimethoxysilane end-capping agent and edge-hydroxylated boron nitride / Huixiang Liu in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 16, N° 5 (09/2019)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 16, N° 5 (09/2019) . - p. 1479-1492 Titre : UV-curable waterborne polyurethane dispersions modified with a trimethoxysilane end-capping agent and edge-hydroxylated boron nitride Type de document : texte imprimé Auteurs : Huixiang Liu, Auteur ; Hong Zhang, Auteur ; Chaohua Peng, Auteur ; Shufan Ren, Auteur ; Conghui Yuan, Auteur ; Weiang Luo, Auteur ; Guorong Chen, Auteur ; Fuqiang He, Auteur ; Lizong Dai, Auteur Année de publication : 2019 Article en page(s) : p. 1479-1492 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosion Caractérisation Nitrure de bore Le nitrure de bore est un composé chimique du bore et de l'azote, de formule chimique brute BN (nombre égal d'atomes de chaque élément). Le nitrure de bore est isoélectronique avec le carbone et, comme ce dernier, existe sous plusieurs formes polymorphiques, dont l'une est analogue au diamant et l'autre au graphite. La forme diamant est l'un des matériaux les plus durs connus et la forme graphite est un lubrifiant apprécié. De plus, ces deux polymorphes possèdent des propriétés d'absorption radar. Polymères à terminaison silane Polymères en émulsion Polyuréthanes Revêtements -- Séchage sous rayonnement ultraviolet Revêtements organiques Surfaces -- Analyse Triméthoxysilane Index. décimale : 667.9 Revêtements et enduits Résumé : In this study, waterborne polyurethane (WPU) dispersions were prepared using a trimethoxysilane end-capping agent (DAA-GPTMS) derived from diallylamine (DAA), (3-glycidoxypropyl)methyldiethoxysilane (GPTMS) and modified with edge-hydroxylated boron nitride (hBN-OH) nanosheets. The WPU films containing DAA-GPTMS possessed remarkable hydrophobicity and favorable water repellency, attaining a contact angle of 101.2° and a 52% decrease in water absorption relative to those of the pure WPU. When the contents of DAA-GPTMS and hBN-OH were 7.5 wt% and 0.2 wt%, respectively, the synergetic effect between the DAA-GPTMS and the hBN-OH nanosheets greatly enhanced the physical and mechanical properties of the nanocomposite films, i.e., the stress doubled and the Young’s modulus increased by fivefold compared to those of pure WPU. Embedding 0.2 wt% of the hBN-OH nanosheets in the WPU coatings resulted in a lower corrosion current density (1.0 × 10−10 A cm−2) and more positive corrosion potential (− 0.63 V). The results demonstrate that WPU/hBN-OH nanocomposite coatings possess great potential for corrosion protection. Note de contenu : - EXPERIMENTAL PROCEDURES : Materials and chemicals - Synthesis of a triethoxysilane end-capping agent (DAA-GPTMS) - Synthesis of hydroxylated hexagonal boron nitride (hBN-OH) - Synthesis of WPU and WPU/hBN-OH nanocomposites - Preparation of the WPU and hBN-OH/WPU nanocomposite films - Characterization - RESULTS : Structural characterization - DLS analysis of WPU and WPU/hBH-OH nanocomposite dispersions - Hydrophobicity and water resistance of WPU and WPU/hBN-OH nanocomposite films - Crosslinking degree of the WPU and WPU/hBN-OH nanocomposite films - Mechanical and physical properties of the WPU and WPU/hBN-OH nanocomposite films - Morphology analysis of the fracture surfaces - Anticorrosion performance DOI : 10.1007/s11998-019-00232-3 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-019-00232-3.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=33026 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
21154	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)