Influence of novel ammonium-modified zinc-free phosphate nanofillers on anticorrosive features of primer-less polyurethane top-coating compositions / Krzysztof Kowalzczyk in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 16, N° 2 (03/2019)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 16, N° 2 (03/2019) . - p. 401-414 Titre : Influence of novel ammonium-modified zinc-free phosphate nanofillers on anticorrosive features of primer-less polyurethane top-coating compositions Type de document : texte imprimé Auteurs : Krzysztof Kowalzczyk, Auteur ; Katarzyna Przywecka, Auteur ; Barbara Grzmil, Auteur Année de publication : 2019 Article en page(s) : p. 401-414 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Anticorrosifs Anticorrosion Electrochimie Essais de brouillard salin Nanoparticules Phosphate d'aluminium Le phosphate d'ammonium est un composé chimique de formule (NH4)3PO4. Il s'agit d'un sel d'ammoniac NH3 et d'acide phosphorique H3PO4, constitué de cations ammonium NH4+ et d'anions phosphate PO43–. Il se forme à l'état de poudre cristalline lorsqu'on mélange deux solutions concentrées d'ammoniac et d'acide phosphorique : 3 NH3 + H3PO4 → (NH4)3PO4. Il est soluble dans l'eau, et la solution aqueuse de phosphate d'ammonium libère de l'ammoniac lorsqu'on la chauffe. Les autres sels d'ammoniac et d'acide phosphorique existent également : phosphate de diammonium (NH4)2HPO4 et phosphate de monoammonium NH4H2PO4. Ils peuvent être convertis l'un en l'autre avec le phosphate d'ammonium en ajoutant davantage d'ammoniac ou d'acide phosphorique selon les besoins. Le phosphate d'ammonium est utilisé dans certains engrais comme source d'azote. Il est également employé comme retardateur de flamme dans la composition des thermoplastiques. Phosphate d'ammonium Phosphate de calcium Phosphate de strontium Phosphate de zinc Polyuréthanes Revêtements protecteurs Index. décimale : 667.9 Revêtements et enduits Résumé : Anticorrosive polyurethane coating compositions were compounded using novel zinc-free nanosized phosphates: aluminum ammonium phosphates (AAP) or calcium aluminum ammonium phosphates (CAAP). For comparison, a nanosized strontium phosphate (SP), AAP/SP mixtures, and a microsized zinc phosphate (ZP) were tested. Paints containing ammonium-modified phosphates exhibited similar or a slightly higher viscosity than systems with SP or ZP. Nevertheless, coatings with the AAP or CAAP reached significantly better gloss and adhesion to a steel substrate as well as a slightly higher hardness. Results of a salt spray test showed that anticorrosive properties of the coatings containing AAP/SP mixtures were markedly better in relation to the systems containing solely AAP, CAAP, SP, or ZP. Electrochemical tests revealed the best barrier/anticorrosive features for AAP (electrochemical impedance spectroscopy and potentiodynamic polarization) or SP and CAAP (a novel electrochemical noise technique). Note de contenu : - Preparation of the anticorrosive polyurethane paints - Test methods DOI : 10.1007/s11998-018-0119-7 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-018-0119-7.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=32412 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20894	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)