Monitoring drying, curing, and thermal properties of acid-catalyzed alkyd-aminoplast wood coatings |
Type de document : |
texte imprimé |
Auteurs : |
Ronald T. Obie, Auteur ; Cameron R. Anderson, Auteur |
Année de publication : |
2024 |
Article en page(s) : |
p. 46-59 |
Note générale : |
Bibliogr. |
Langues : |
Américain (ame) |
Catégories : |
Aminoplastes Les aminoplastes sont les polymères thermodurcissables les plus répandus, devançant les polyuréthanes.
On distingue deux types principaux, les résines urée-formaldéhyde (sigle UF) et mélamine-formaldéhyde (MF). Leur synthèse, qui utilise le méthanal, s'apparente à celle des phénoplastes.
- Synthèse :
Ils sont obtenus par une réaction de polycondensation à partir du comonomère formaldéhyde, le second comonomère portant des groupes amino- -NH2. Suivant la nature chimique de ce dernier, on distingue deux types de précurseurs d'aminoplastes :
- Les "résines urée-formaldéhyde" ou "urée-formol" (UF) utilisent l'urée, molécule tétravalente. Elles représentent environ 80 % du tonnage des aminoplastes (en 2000) et sont relativement bon marché.
- Les "résines mélamine-formaldéhyde" ou "mélamine-formol" (MF) sont issues de la mélamine. L'hexavalence de ce composé peut permettre la formation de réseaux denses. Elles sont surtout connues sous le nom commercial Formica. Elles représentent environ 17 % du tonnage des aminoplastes et sont plus chères que les précédentes. (Wikipedia) Bois -- Revêtements protecteurs Catalyse Polyalkydes Réticulation (polymérisation) Revêtement en phase solvant Revêtements -- Propriétés mécaniques Revêtements -- Propriétés thermiques Revêtements organiques
|
Index. décimale : |
667.9 Revêtements et enduits |
Résumé : |
Fast-curing acid-catalyzed alkyd-aminoplast coatings are often utilized as protective coatings for wood cabinet coatings. Quantitative assessment of impact of resin, crosslinker, and catalyst concentration on the curing process can be challenging for these and other coatings as well.
In the development of these coatings, curing is often assessed after the coating film has been exposed to a given cure profi le by evaluation of physical properties such as hardness development as a function of time after exiting an oven. Curing under ambient conditions is often assessed by evaluating coating hardness development as a function of ambient drying-time conditions.
Evaluation of the infl uence of solvent on cure and crosslinking is often assessed by means of the finger-touch-down method as the sample is drying. Although these methods are very useful, they do not give quantitative insight into the drying and curing of the coating during the early drying process.
The current work investigates the eff ect of resin and crosslinker composition, and catalyst concentration, on the kinetics of curing of solvent-based acid catalyzed alkyd-aminoplast wood coatings.
Further, the research investigates dynamic mechanical thermal properties of the resulting coatings after exposure to a given cure profile. |
Note de contenu : |
- Assessment of curing
- Experimental : Evaporative dynamic oscillation (EDOT) - Automated dynamic drying time - Hardness of drying and/or cured films
- Results and Discussion : Impact of PTSA acid catalyst concentration on cure rate of an acid-catalyzed varnish |
En ligne : |
https://drive.google.com/file/d/1aZHSiSKDh7RUUFXCzV56ie85IXGLb1nC/view?usp=drive [...] |