Improved corrosion resistance and hydrophobic stability of sol-gel coatings by benzoxazine modification on aluminum alloys AA1060 |
| Type de document : |
texte imprimé |
| Auteurs : |
Zhou Zhou, Auteur ; Juan Liu, Auteur ; Xin Meng, Auteur ; Changlu Zhou, Auteur |
| Année de publication : |
2024 |
| Article en page(s) : |
p. 893-905 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Aluminium -- Alliages
Anticorrosifs
Anticorrosion
Benzoxazine
Caractérisation
Hydrophobie
Métaux -- Revêtements protecteurs
Revêtements organiques
Silanes
Sol-gel, Procédé
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
A series of sol-gel coatings based on tetraethoxysilane (TEOS) was adopted in order to provide corrosion protection for aluminum alloys AA1060, which were modified by incorporating various ratios of silane-functionalized benzoxazine (Bz), labeled as Bz-based sol–gel coatings. Fourier transform infrared spectra were utilized to characterize the crosslinking network of Bz-based sol–gel coatings through calculating the conversion of Bz structure after the curing process, which was also further confirmed by the gel content test. Both hydrophobicity and corrosion resistance of Bz-based sol–gel coatings were fully investigated with the assistance of water contact angle (WCA) measurements, electrochemical impedance spectroscopy (EIS), and salt spray test. Bz incorporation could improve hydrophobic stability and corrosion resistance of Bz-based sol–gel coatings with increasing the Bz content during the 30-day immersion in a 3.5 wt% NaCl aqueous solution. Better performance of Bz-based sol–gel coatings than that of a control TEOS coating with a WCA above 93° and a charge-transfer resistance over 100 kΩ cm2 after 30-day EIS measurement shows their effective protective property for aluminum alloys. |
| Note de contenu : |
- EXPERIMENTAL : Chemicals - Synthesis of Bz monomer - Surface treatment of aluminum alloys - Preparation of Bz-based sol-gel coatings - Characterization
- RESULTS AND DISCUSSION : Crosslinking structures of Bz-based sol-gel coatings - Hydrophobicity of Bz-based sol-gel coatings - Corrosion resistance behaviors of Bz-based sol-gel coatings |
| DOI : |
https://doi.org/10.1007/s11998-023-00858-4 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007/s11998-023-00858-4.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=41065 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 21, N° 3 (05/2024) . - p. 893-905
Aller sur edunet
Accueil
Improved corrosion resistance and hydrophobic stability of sol-gel coatings by benzoxazine modification on aluminum alloys AA1060 in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 21, N° 3 (05/2024)