Facile fabrication of superhydrophilic and underwater superoleophobic chitosan–polyvinyl alcohol-TiO2 coated copper mesh for efficient oil/water separation / Qiuying You in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 15, N° 5 (09/2018)  

[article]  inJOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 15, N° 5 (09/2018) . - p. 1013-1023 Titre : Facile fabrication of superhydrophilic and underwater superoleophobic chitosan–polyvinyl alcohol-TiO2 coated copper mesh for efficient oil/water separation Type de document : texte imprimé Auteurs : Qiuying You, Auteur ; Guoxia Ran, Auteur ; Chan Wang ; Yuan Zhao ; Qijun Song Année de publication : 2018 Article en page(s) : p. 1013-1023 Note générale : Bibliogr. Langues : Américain (ame) Catégories : Alcool polyvinylique Anticorrosion Chitosane Le chitosane ou chitosan est un polyoside composé de la distribution aléatoire de D-glucosamine liée en ß-(1-4) (unité désacétylée) et de N-acétyl-D-glucosamine (unité acétylée). Il est produit par désacétylation chimique (en milieu alcalin) ou enzymatique de la chitine, le composant de l'exosquelette des arthropodes (crustacés) ou de l'endosquelette des céphalopodes (calmars...) ou encore de la paroi des champignons. Cette matière première est déminéralisée par traitement à l'acide chlorhydrique, puis déprotéinée en présence de soude ou de potasse et enfin décolorée grâce à un agent oxydant. Le degré d'acétylation (DA) est le pourcentage d'unités acétylées par rapport au nombre d'unités totales, il peut être déterminé par spectroscopie infrarouge à transformée de Fourier (IR-TF) ou par un titrage par une base forte. La frontière entre chitosane et chitine correspond à un DA de 50 % : en deçà le composé est nommé chitosane, au-delà, chitine. Le chitosane est soluble en milieu acide contrairement à la chitine qui est insoluble. Il est important de faire la distinction entre le degré d'acétylation (DA) et le degré de déacétylation (DD). L'un étant l'inverse de l'autre c'est-à-dire que du chitosane ayant un DD de 85 %, possède 15 % de groupements acétyles et 85 % de groupements amines sur ses chaînes. Le chitosane est biodégradable et biocompatible (notamment hémocompatible). Il est également bactériostatique et fongistatique. Le chitosane est également utilisé pour le traitement des eaux usées par filtration ainsi que dans divers domaines comme la cosmétique, la diététique et la médecine. Cuivre Hydrophilie Maille métallique Membranes (technologie) Mouillabilité Nanoparticules Oléophobie Résistance à l'abrasion Séparation huile/eau Index. décimale : 667.9 Revêtements et enduits Résumé : Organic–inorganic hybrid membranes are attractive material for oil/water separation. Here, a hydrophilic and oleophobic membrane was prepared by coating chitosan (CTS) and polyvinyl alcohol (PVA) on the surface of copper mesh using glutaraldehyde (GA) as crosslinking agent. After introduction of TiO2 nanoparticles, the surface roughness of the composite film was increased and a superhydrophilicity and underwater superoleophobicity surface was obtained due to the enhancement in wettability. The as-prepared superhydrophilic membrane was characterized by SEM, FTIR, XRD, and its surface wetting behavior was measured by contact angle meter. The effect of CTS, PVA, GA, and TiO2 on the microstructure, underwater oil contact angle, and sliding angle was comprehensively evaluated. Then, the super hydrophilic membrane was used for oil/water separation, a separation efficiency (> 99.7%) was obtained with a flux rate of 16,000 L m−2 h−1. The intrusion pressures for all tested oils that the membrane can support are above 1.0 kPa. Significantly, the super hydrophilic membrane exhibited good antiabrasion and anticorrosive properties. After repeated use for 60 times, the separating performances and average permeate fluxes showed no obvious degradation. Note de contenu : - EXPERIMENTAL SECTION : Chemicals and materials - Fabrication of CTS-PVA-TiO2 coated copper mesh - Instruments and methods - Oil/water separation experiment - RESULTS AND DISCUSSION : Components and morphology of coated mesh - Surface wettability of coated mesh - Oil/water separation experiments - Stability and anticorrosive property of coated mesh DOI : 10.1007/s11998-017-0036-1 En ligne : https://link.springer.com/content/pdf/10.1007%2Fs11998-017-0036-1.pdf Format de la ressource électronique : Pdf Permalink : https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=31125 [article]

Réservation

Réserver ce document

Exemplaires (1)

Code-barres	Cote	Support	Localisation	Section	Disponibilité
20232	-	Périodique	Bibliothèque principale	Documentaires	Disponible

---

1 (1 - 1 / 1)